Electronic Structures, Magnetic Properties, Half-Metallicity and Optical Properties of the Zincblende Zn1−xMoxS
Zhu-Hua Yin,Jian-Min Zhang,Ke-Wei Xu
DOI: https://doi.org/10.1016/j.jmmm.2015.10.121
IF: 3.097
2016-01-01
Journal of Magnetism and Magnetic Materials
Abstract:The electronic structures, magnetic properties, half-metallicity and optical properties of Zn1-xMoxS (x=0.00, 0.25, 0.50, 0.75, 1.00) are studied by spin-polarized first-principles calculation. Excepting the Zn0.5Mo0.5S system with a tetragonal structure, the other systems Zn1-xMoxS (x=0.00, 0.25, 0.75, 1.00) are all in the cubic structure. The lattice constants (volumes) of the Mo doped systems are larger than those of the pure ZnS due to the atomic radius of 2.01Å for Mo atom larger than that of 1.53Å for Zn atom. Although pure ZnS is a nonmagnetic semiconductor with a wide band gap of 3.12eV, due to incompletely filled Mo-4d orbital both the moderate Mo doped systems Zn0.5Mo0.5S and Zn0.25Mo0.75S are magnetic metal, especially the less Mo doped system Zn0.75Mo0.25S and the completely Mo doped system MoS are magnetic half-metal. For Zn0.75Mo0.25S system with a magnetic half-metal character as one example, the conducted spin-up channel is only contributed by the threefold degenerate t2g(dxy,dyz,dzx) states due to the tetrahedral crystal field of the S atoms pushing the spin-up channel of the double degenerate eg(dz2,dx2-y2) states down below the Fermi level EF. Mo doping not only influences the shape of the original broad absorption peak ranging from 2.5 to 20eV of pure ZnS, but also leads to two new narrow absorption peaks appeared in the ranges from 0 to 3eV and from 33 to 43eV. Moreover, their maximum absorption rate and the corresponding energy increase with increasing Mo content. These results are very useful for Zn1-xMoxS to be applied in optical detectors and spintronics devices.