Giant Electrocaloric Effect and Ultrahigh Refrigeration Efficiency in Antiferroelectric Ceramics by Morphotropic Phase Boundary Design
Junjie Li,Jianting Li,Hong-Hui Wu,Shiqiang Qin,Xiaopo Su,Yu Wang,Xiaojie Lou,Dong Guo,Yanjing Su,Lijie Qiao,Yang Bai
DOI: https://doi.org/10.1021/acsami.0c13734
2020-09-14
Abstract:Electrocaloric effect (ECE) in ferroelectric (FE)/antiferroelectric (AFE) materials offers a promising high-efficient and zero-emission solid-state cooling technology, whose materials design is usually focused on the morphotropic phase boundary (MPB) between two FE phases. This work constructs an MPB between an orthorhombic AFE and a rhombohedral FE phase in Pb<sub>0.97–<i>x</i></sub>Ba<sub><i>x</i></sub>La<sub>0.02</sub>Zr<sub>0.95</sub>Ti<sub>0.05</sub>O<sub>3</sub> (PBLZT100<i>x</i>, <i>x</i> = 0–0.08) ceramics and achieves a superior ECE performance. An unprecedented high electrocaloric strength of 1.52 K·mm/kV and an ultrahigh refrigeration efficiency (coefficient of performance = 16) are obtained in PBLZT4, in the MPB near AFE end. Moreover, a large negative ECE, with the highest strength up to −0.41 K·mm/kV, is also realized due to the electric field-induced AFE–FE transition. The coexistence of giant positive and negative ECEs at adjacent temperatures can further improve the cooling capacity (∼17%) of solid-state refrigeration in a well-designed cooling cycle. This work provides a brand new materials design strategy to achieve giant positive and negative ECEs simultaneously and a novel cooling cycle to efficiently utilize the two effects.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c13734?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c13734</a>.Tolerance factors for PbZrO<sub>3</sub>, PZT, and PBLZT ceramics, XRD patterns for PBLZT ceramics, electric hysteresis behaviors for PBLZT ceramics, microstructures for as-sintered PBLZT4, PBLZT4.8, PBLZT6, and PBLZT8 ceramics, temperature dependences of dielectric and heat properties for PBLZT ceramics, ECE results obtained by direct measurement, temperature dependence of polarization under selected electric fields for PBLZT ceramics, temperature dependence of pyroelectric coefficient under selected electric fields for PBLZT ceramics, temperature dependence of ECE Δ<i>T</i> under different electric fields indirectly calculated based on the Maxwell relation, ECE heat flow at 100 °C for PBLZT4 ceramics, ECE Δ<i>T</i> (by direct measurements) and polarization current as a function of electric field change Δ<i>E</i> at different temperatures for PBLZT4 ceramics, theoretical calculation of polarization and free energy in AFE using GLD phenomenology, and mass density of PBLZT ceramics (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c13734/suppl_file/am0c13734_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology