Tunable luminescence in transparent oxyfluoride glass–ceramics containing KY3F10: Mn2+/Eu3+ nanocrystals for highly sensitive temperature sensing
Junyi Ying,Lizhi Fang,Xiong Zhou,Haiping Xia,Hongwei Song,Baojiu Chen
DOI: https://doi.org/10.1007/s10854-024-13175-2
2024-07-18
Journal of Materials Science Materials in Electronics
Abstract:Transparent glass–ceramics (GCs) encompassing Mn 2+ /Eu 3+ -doped KY 3 F 10 (Mn 2+ /Eu 3+ : KY 3 F 10 ) nanocrystals were fabricated successfully using the traditional method of melt-quenching. The Mn 2+ and Eu 3+ ions were confirmed incorporated in the lattices of Y 3+ in KY 3 F 10 nanocrystals determining from the results of change of emission intensity of Eu 3+ and Mn 2+ , EDS, and TEM before and after micro-crystallization of glass. When Mn 2+ was fixed at 0.5 mol% in concentration and Eu 3+ was changed from 0 to 0.9 mol%, the emission color of the GCs was varied from green to yellow–orange and the average lifetime of Mn 2+ ion was reduced from 8.61 to 7.38 ms. As Eu 3+ concentration increases, the efficiency of energy transfer from the excited states of Mn 2+ ions to Eu 3+ ions rises, resulting in enhanced Eu 3+ emission and diminished Mn 2+ emission, thereby causing a change in emission color and a reduction in the lifetime of Mn 2+ ions. An absolute sensitivity ( S a ) reaching up to 0.25% K −1 at 298 K and a relative sensitivity ( S r ) of 0.62% K −1 at 298 K were derived by analyzing the fluorescence intensity ratio (FIR) between 540 nm of Mn 2+ and 613 nm of Eu 3+ ions. The transparent GCs with physico-chemical stability and good luminous efficiency have application prospects for multicolor display applications and temperature sensors.
materials science, multidisciplinary,engineering, electrical & electronic,physics, applied, condensed matter