Abstract:Carboxymethyl chitosan-graft-polylactide (CMCS-PLA) and carboxymethyl chitosan (CMCS) hydrogels were prepared by using 1-(3-dimethylaminopropyl)-3-ethylcarbodiimide hydrochloride/N-hydroxysuccinimide (EDC/NHS) as crosslinking agent and catalyst at room temperature. The biocompatibility of the hydrogels was evaluated with the aim of assessing their potential as drug carrier. Various aspects of biocompatibility were considered, including MTT assay, agar diffusion test, release of lactate dehydrogenase (LDH), hemolytic test, plasma recalcification time (PRT), and dynamic clotting time. MTT assay showed that the cytotoxicity level of both hydrogels to L-929 cells was 0 or 1. The LDH release of CMCS and CMCS-PLA was 26 and 29%, respectively, which is slightly higher than that of the negative control (21%) and much lower than that of the negative control (87%). The hemolysis ratio of CMCS and CMCS-PLA was 1.4 and 1.7%, respectively, suggesting outstanding anti-hemolysis properties of both materials. The PRT value of CMCS and CMCS-PLA was higher by 77 and 99% than the value of the positive control. All the results revealed that the hydrogels present good cytocompatibility and hemocompatibility in vitro. In vivo degradation and tissue compatibility were evaluated by subcutaneous injection in the dorsal area of rats. CMCS and CMCS-PLA hydrogels were completely degraded and the inflammatory response also completely disappeared around hydrogels after 19 days in vivo. It is thus concluded that hydrogels formed of CMCS and CMCS-PLA with outstanding biocompatibility are promising as potential drug carrier.

Preparation, Blood Coagulation and Cell Compatibility Evaluation of Chitosan-Graft-polylactide Copolymers.

Preparation of biocompatible chitosan grafted poly(lactic acid) nanoparticles.

Preparation and Cytocompatibility of Chitosan‐modified Polylactide

A Facile Method for Preparing Biodegradable Chitosan Derivatives with Low Grafting Degree of Poly(lactic Acid).

Preparation and Characterization of Chitosan and Lactide Grafted Polymerization Materials

A study on cytocompatible poly(chitosan-g-?-lactic acid)

Preparation of Chitosan-G-polylactide Graft Copolymers Via Self-Catalysis of Phthaloylchitosan and Their Complexation with DNA

Preparation of fully bio-based multilayers composed of heparin-like carboxymethylcellulose sodium and chitosan to functionalize poly (l-lactic acid) film for cardiovascular implant applications

Preparation and Blood Compatibility of Electrospun Nanofibrous CTS/PLA Mats from Chitosan Nanopowders and Poly(lactic Acid)

Novel Bioresorbable Hydrogels Prepared From Chitosan-Graft-Polylactide Copolymers

Synthesis and Characterization of Chitosan-Graft-poly(lactic Acid) Copolymer

t Preparation of Chitosan-g-Polylactic acid and the Study of its Crosslinked film

Preparation and Degradation Properties of Hydroxyethyl Chitosan-g-Poly(D,L-Lactide) Copolymers

The Synthesis and Properties of Poly(L-Lactide)-Chitosan Graft Copolymer

Preparation of Hydrophilic Poly(L-Lactide) Electrospun Fibrous Scaffolds Modified with Chitosan for Enhanced Cell Biocompatibility

Preparation and Biological Evaluations of PLA/chitosan Composite Materials

One-step Synthesis of Amino-Reserved Chitosan-Graft-polycaprolactone As a Promising Substance of Biomaterial

Synthesis and Characterization of Chitosan-Graft-polycaprolactone Copolymers

Biocompatibility and in vivo degradation of chitosan based hydrogels as potential drug carrier.

Preparation and Degradation Properties of Hydroxyethyl Chitosan-<i>g</i>-Poly(<i>D,L</i>-Lactide) Copolymers

Biocompatibility of Poly(ε-caprolactone) Scaffold Modified by Chitosan—The Fibroblasts Proliferation in vitro