Abstract:A key point for the development of a renewable energy economy at a large scale is the possibility to use the current natural gas network and storage capacity to transport and store hydrogen. This study is dedicated to evaluate the integrity of materials used for underground aquifer storage regarding hydrogen embrittlement in a gaseous environment saturated with water vapour and containing few amounts of H 2 S. In this environment, the water vapour content in the gas stored may reach saturation at bottom well pressure and temperature. It is known that the presence of impurities in the gas, such as H 2 O, can promote or inhibit hydrogen embrittlement phenomenon, depending on the nature of the steel. This work investigates mechanical properties of a tempered martensite N80-Q steel, and a ferrite-perlite L360-NB C–Mn steel issued from a completion and a collect tube respectively. The testing environments are NG, NG + H 2 S, NG + 25%H 2 and NG + 25%H 2 + H 2 S saturated in water vapour at 8.5 MPa and room temperature. These environmental conditions aim at replicating the storage service conditions. Fracture toughness and fatigue crack growth properties are assessed. So far, the mechanical behaviour of such steels under hydrogen gas pressure saturated with water vapour and low amount of H 2 S has poorly been addressed. Regarding toughness properties, the two steels present different behaviour: for the L360 NB crack has not propagated for any testing environments, while cracks propagated in all the tests for the N80 Q. Despite this difference, for the two steels, the toughness does not seem to be affected by hydrogen as the results obtained in NG + 25%H 2 + H 2 O and NG + H 2 O are similar. Based on the literature C–Mn steels toughness is affected by the presence of dry hydrogen. Hence, the results presented here show that H 2 O inhibits hydrogen embrittlement as far as toughness is concerned. The L360NB, however, presented a slight decrease in toughness properties with the combination of NG + 25%H 2 + H 2 S + H 2 O. FCG (fatigue crack growth) results, on the opposite, clearly highlight the influence of hydrogen on the mechanical behaviour of the two steels. The FCG rates are faster from a factor five (resp. 10) in NG + 25%H 2 + H 2 O compared to NG + H 2 O for the N80 Q (resp. L360). In this article, toughness and FGC results on the two steels are discussed in terms of microstructure and mechanical loading modes, aiming to quantify and better understand the influence of H 2 O and H 2 S on the sensitivity of low alloy steels to hydrogen embrittlement.

Comparison of tensile and impact behavior of carbon steel in H2S environments

Effect of H2S Corrosion on the Fracture Toughness of the X80 Pipeline Steel Welded Joint

Experimental study on slow tensile, fatigue, and impact on X42 steel and #20 carburizing steel

Unraveling the effect of H2S on the corrosion behavior of high strength sulfur-resistant steel in CO2/H2S/Cl− environments at ultra high temperature and high pressure

Insights into the effect of H2S on the corrosion behavior of N80 steel in supercritical CO2 environment

Effect of Ti Microalloying on the Corrosion Behavior of Low-Carbon Steel in H2S/CO2 Environment

Effect of H2S concentrations on corrosion failure of L245NS steel in CO2-O2-H2S system

Effect of interaction between corrosion film and H2S/CO2 partial pressure ratio on the hydrogen permeation in X80 pipeline steel

Combined effect of hydrogen embrittlement and corrosion on the cracking behaviour of C110 low alloy steel in O2-contaminated H2S environment

Effects of Adding CO2 to Low Level H2S Containing Aqueous Environments on the Corrosion and Hydrogen Penetration Behaviors of High-Strength Steel

Different Effects of Pure Hydrogen Vs. Hydrogen/natural Gas Mixture on Fracture Toughness Degradation of Two Carbon Steels

Hydrogen embrittlement of X80 pipeline steel in H 2 S environment: Effect of hydrogen charging time, hydrogen-trapped state and hydrogen charging–releasing–recharging cycles

Effect of Hydrostatic Pressure on Hydrogen behavior on the surface of X70 pipeline steel

INFLUENCE OF SATURATED H_2S ON CORROSION BEHAVIOR OF 316L STAINLESS STEEL

Effect of H2S on CO2 Corrosion of Mild Steel in High Temperature Supercritical CO2 Condition

Comparative evaluation on hydrogen damage behavior of two martensitic high strength press hardening steels

Role of microstructure heterogeneity on hydrogen-assisted fracture toughness degradation of X80 weld metal in H 2 S-saturated solution

Effect of tensile stress on the hydrogen adsorption of X70 pipeline steel

Effect of water vapour and H 2 S content on the hydrogen embrittlement sensitivity of low alloy steels for underground storage

Effect of carbon dioxide on corrosion of tubular steel in high hydrogen sulfide and carbon dioxide environments

Synergistic effect of different testing environments on the hydrogen-induced mechanical degradation to establish the role of microstructural features on the failure of X70 pipeline steel