Abstract:Herein, the evolution of ZnO structures from hexagonal disk to prismoid, prism and pyramid was found via a facile two-step low temperature hydrothermal reaction, and the evolution was achieved by only adjusting the pH value of the reactive solution without the assistance of a template or a surfactant. The characterization results showed that the precursor (hexagonal Zn-5(OH)(8)Cl-2 center dot 2H(2)O disk) played a key role in the morphology evolution of ZnO during the early stage of the growth process and that the disks tended to stack together layer by layer in both directions (up and down) to form prismoid, prism and pyramid structures with the increase in pH value from 7 to 10. After calcination, the corresponding hexagonal ZnO microstructures were obtained. This structure evolution resulted in the weakening dominance of the (0001) plane in the total exposed crystal facets. Furthermore, despite the similar specific surface areas of the four hexagonal ZnO microstructures, the gas sensing properties of the sensors based on these microstructures deteriorated sequentially. At a working temperature of 330 degrees C, the ZnO disk with the most exposed (0001) plane showed the highest gas response toward ethanol, which was nearly 2, 3, and 6 times higher than those of the prismoid, prism and pyramid structures, respectively. This superior gas sensing performance strongly depends on the predominantly exposed polar facets (0001), which can provide more active sites for oxygen adsorption and subsequent reaction with the detected gas than other apolar facets. It demonstrates that the (0001) crystal facet plays a significant role in the gas sensing behavior of ZnO. This research will bring some inspiration to researchers for the fabrication of a high performance ZnO gas sensor as well as other metal oxides.

Effect of Different Structures on the Gas Sensing Property of ZnO

Hydrothermal Synthesis and Growth Mechanisms of Different ZnO Nanostructures and Their Gas-Sensing Properties

Gas-sensing performance enhancement in ZnO nanostructures by hierarchical morphology

Gas-sensing Property Improvement of ZnO by Hierarchical Flower-Like Architectures

Gas Sensing Properties of ZnO-SnO2 Nanostructures.

Controlled ZnO hierarchical structure for improved gas sensing performance

Self-assembly of ZnO Nanosheets into Flower-Like Architectures and Their Gas Sensing Properties

Different morphologies of ZnO nanorods and their sensing property

Effect of Zinc Doping on Microstructures and Gas-Sensing Properties of Sno2 Nanocrystals

Synthesis of hierarchical ZnO nanostructure assembled by nanorods and their performance for gas sensing

Nanostructures and Sensing Properties of ZnO Prepared Using Normal and Oblique Angle Deposition Techniques

Flower-like Hierarchical Zinc Oxide Architectures: Synthesis and Gas Sensing Properties

One-Dimensional Zinc Oxide Decorated Cobalt Oxide Nanospheres for Enhanced Gas-Sensing Properties

Evolution of ZnO microstructures from hexagonal disk to prismoid, prism and pyramid and their crystal facet-dependent gas sensing properties

Chemical Vapor Deposition Preparation of Nanostructured ZnO Particles and Their Gas-Sensing Properties

Controllable Preparation and Gas Sensing Performance of Nanosized ZnO with Different Micromorphologies

An Evolution From 3d Face-Centered-Cubic Znsno3 Nanocubes To 2d Orthorhombic Znsno3 Nanosheets With Excellent Gas Sensing Performance

The Effect Microstructure on the Gas Properties of Ag Doped Zinc Oxide Sensors: Spheres and Sea-Urchin-like Nanostructures

Structure and Acetylene Sensing Behavior of Zinc Oxide Nanowires Based Gas Sensor

Hmt Assisted Hydrothermal Synthesis of Various Zno Nanostructures: Structure, Growth and Gas Sensor Properties