Abstract:b Through the ring-opening polymerization of L-lactide initiated by hydroxyl groups on the surface of HNTs using stannous 2-ethylhexanoate as catalyst, halloysite nanotubes surface-grafted with poly (L-lactic acid) (PLLA) segments (g-HNTs) were synthesized. The compositions and morphologies of the modified and unmodified HNTs were observed by Fourier transformation infrared (FTIR), thermal gravimetric analysis (TGA) and transmission electron microscopy (TEM). Then, a series of PLLA, PLLA/HNTs and PLLA/g-HNTs nanofiber membranes were prepared by electrospinning, the influences of the spinning conditions on the morphologies of the nanofiber membranes were discussed, and the composition, micrograph, interfacial compatibility, tensile properties and cellular compatibility of the composite membranes were studied too. Results showed that the grafting percentage of PLLA segments on the surface of g-HNTs was 14.22% as the molar ratio of HNTs to L-lactide was 1:10. The tubular morphology of HNTs changed little after surface grafting, and g-HNTs can easily disperse in anhydrous ethanol. The voltage and the feed rate have effects on the morphology of fiber membranes, when the voltage was 15 kV and feed rate was 1 mL/h, the diameter of the electrospinning fiber was relatively uniform. The dispersion and interfacial compatibility of g-HNTs in PLLA matrix were superior to those of pristine HNTs, when the content of g-HNTs increased up to 40 wt%, the fiber micrograph of the PLLA/g-HNTs composite membranes continues to remain good, and continuous and relatively uniform fiber can be got. With the content of HNTs and g-HNTs increased, the tensile strength and modulus increased first and then decreased, as the filler content was 5 wt%, the highest tensile strengths and moduli were obtained for both of the PLLA/HNTs and PLLA/g-HNTs composite nanofiber membranes. However, the tensile strength and modulus of the PLLA/g-HNTs composite nanofiber membranes were always higher than those of PLLA/HNTs composite nanofiber membranes at all filler contents due to the good adhesive strength between the g-HNTs and PLLA matrix. The results of 3T3 cells culture in vitro indicated that the cellular compatibility of the PLLA/g-HNTs composite nanofiber membranes is very good, and better than that of pure PLLA and PLLA/HNTs nanofiber membranes.

Electrospun Plga/Multi-Walled Carbon Nanotubes/Wool Keratin Composite Membranes: Morphological, Mechanical, and Thermal Properties, and Their Bioactivities in Vitro

Electrospun Aligned PLLA/PCL/functionalised Multiwalled Carbon Nanotube Composite Fibrous Membranes and Their Bio/mechanical Properties

Hybrid Nanofibrous Membranes of Plga/Chitosan Fabricated Via an Electrospinning Array

Composite Fibrous Membranes of Plga and Chitosan Prepared by Coelectrospinning and Coaxial Electrospinning

Electrospun PCL/gelatin Composite Nanofiber Structures for Effective Guided Bone Regeneration Membranes

A Nanofibrous Composite Membrane of PLGA–chitosan/PVA Prepared by Electrospinning

Biomimetic Synthesis of Poly(Lactic-Co-Glycolic Acid)/Multi-Walled Carbon Nanotubes/Apatite Composite Membranes

Electrospun poly-L-lactic acid/β-tricalcium phosphate composite nanofiber membranes

Improved Biological Characteristics of Poly(l-Lactic Acid) Electrospun Membrane by Incorporation of Multiwalled Carbon Nanotubes/hydroxyapatite Nanoparticles.

Degradation of Electrospun PLGA-chitosan/PVA Membranes and Their Cytocompatibility in Vitro.

Morphological, Mechanical and Thermal Properties of Poly(lactic acid) (PLA)/Cellulose Nanofibrils (CNF) Composites Nanofiber for Tissue Engineering

Electrospun Composite Nanofiber Membrane of Poly( L -Lactide) and Surface Grafted Chitin Whiskers: Fabrication, Mechanical Properties and Cytocompatibility

Fabrication and Cell Culturing on Carbon Nanofibers/Nanoparticles Reinforced Membranes for Bone-Tissue Regeneration

Electrospun Poly(lactic-Co-glycolic Acid)/wool Keratin Fibrous Composite Scaffolds Potential for Bone Tissue Engineering Applications

Solvent-free Cellulose Nanocrystal Fluids for Simultaneous Enhancement of Mechanical Properties, Thermal Conductivity, Moisture Permeability and Antibacterial Properties of Polylactic Acid Fibrous Membrane

Preparation of PLLA/g-HNTs Composite Nanofiber Membranes by Electrospinning and Studies on Their Properties

A Quaternary Composite Fiber Membrane for Guided Tissue Regeneration

Electrospun preparation and biological properties in vitro of polyvinyl alcohol/sodium alginate/nano-hydroxyapatite composite fiber membrane

Electrospun Poly (Lactic-Co-glycolic Acid)/Multiwalled Carbon Nanotubes Composite Scaffolds for Guided Bone Tissue Regeneration

Characterization of Electrospun Core/shell Poly(vinyl Pyrrolidone)/poly(l-Lactide-co-ε-caprolactone) Fibrous Membranes and Their Cytocompatibility in Vitro

PLLA/Graphene Nanocomposites Membranes with Improved Biocompatibility and Mechanical Properties