Low-temperature Reactive Hot-Pressing of Cerium-Doped Titanate Composite Ceramics and Their Aqueous Stability

Yuancheng Teng,Shanlin Wang,Yi Huang,Kuibao Zhang

DOI: https://doi.org/10.1016/j.jeurceramsoc.2013.10.020

IF: 5.7

2014-01-01

Journal of the European Ceramic Society

Abstract:Reactive hot-pressing was scarcely applied to fabricate titanate ceramic waste forms designed for immobilizing high-level radioactive waste (HLW). However, compared with non-reactive processes, there is an advantage of producing high-density ceramics at reduced temperatures by reactive hot-pressing. CeIV-doped titanate composite ceramics with relative densities in excess of 99% were prepared by reactive hot-pressing at temperature as low as 1150°C and pressure of 30MPa for 1–4h. The results show that low-temperature densification of the composite ceramics might be attributed to the plastic deformation under hot-pressing condition. In addition, aqueous stability testing was carried out using the standard MCC-1 static leach test method. The results demonstrate that the normalized elemental leach rate of Ca, Ce and Zr were fairly constant in a low value below 5×10−2gm−2d−1, 7×10−6gm−2d−1 and 6×10−6gm−2d−1 after 21d.