Effect of Phosphorus Doping on Conductivity, Diffusion, and High Rate Capability in Silicon Anode for Lithium-Ion Batteries
Bo Long,Youlan Zou,Zhaoyang Li,Zengsheng Ma,Wenjuan Jiang,Haiyan Zou,Hengyue Chen
DOI: https://doi.org/10.1021/acsaem.0c00534
IF: 6.4
2020-05-12
ACS Applied Energy Materials
Abstract:Poor long-term cycling stability and rate capability seriously restricted the commercial applications of silicon (Si) anodes, because of the huge volume change and the kinetic problems linked to the electronic conductivity and solid-state diffusion of Li+. To overcome these challenges, herein, heteroatom phosphorus (P), as the dopant, is successfully incorporated with silicon to form coral-like P-doped Si anode in lithium-ion batteries. Such the coral-like P-doped Si anode exhibits a noticeable specific capacity (2460.4 mA h g–1 at 0.2 A g–1), excellent rate capability (911 mA h g–1 at 16 A g–1), and long cycling stability (1564 mA h g–1 after 100 cycles at 2 A g–1), which are attributed to three factors: (1) the three-dimensional interconnected nanopores of the coral-like P-doped Si could accommodate volume expansion during cycling; (2) P doping improves the electron-donating ability and suppresses the polarization effect; (3) low activation energies and high Li+ diffusion coefficient are mapped and calculated from the nano- to micrometer and macroscales, verifying that the high Li+ diffusion facilitates the redox kinetics of Si species.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.0c00534.Scheme S1, two possible reaction pathways for the formation of generation of P–(O–Si)n bonds; Figure S1, SEM images of (a) pure SiO2, (b) HRTEM image of P0.125Si, (c) TEM images of pure Si; Table S1, atom contents of P0.063Si, P0.125Si, and P0.188Si samples from XPS measurements (at. %); Table S2, fitting parameters for XPS Si 2p core-level spectra of P0.063Si, P0.125Si, and P0.188Si samples: binding energy and corresponding normalized intensity; Figure S2 N2 adsorption/desorption isotherms and corresponding pore size distribution curves; Figure S3, the equivalent circuit for fitting the impedance spectra of pure Si, P0.063Si, P0.125Si, and P0.188Si electrodes; Table S4, simulation results of the kinetic parameters of Si, P0.063Si, P0.125Si, and P0.188Si electrodes before and after 10 cycles; preparation of the electrodes for ESM testing; electrochemical performance of Si and different kinds of P-doped Si (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels