Abstract:Electroless nickel composite coatings have the potential for high-temperature tribological applications, and a combination of high wear resistance and low friction factor is one of the desirable solutions but still a tricky problem. The addition of self-lubricating WS2 and hard Si3N4 nanoparticles to the Ni-P coatings is expected to obtain good high-temperature tribological performance. In this work, Ni-P-Si3N4-WS2 composite coatings with various contents of WS2 nanoparticles were prepared using electroless plating and subsequently annealed at 400 °C in an inert atmosphere. The tribological properties of the coatings were evaluated using a ball-on-disc wear instrument at operating temperatures from 25 to 600 °C. The microstructure, chemical composition, and surface morphology of the coatings were characterized by X-ray diffractometry (XRD), energy disperse spectroscopy (EDS), and scanning electron microscopy (SEM). Upon increasing the WS2 dosage in the bath, the WS2 content in the coating increased and the micro-hardness of the as-plated coating increased from 539 to 717 HV. After heat treatment, the coating underwent a crystallization process, and the hardness increased from 878 to 1094 HV. The main wear mechanism of the coating changed from adhesive wear in the as-plated state to abrasive wear in the annealed state. The annealed Ni-P-Si3N4-WS2 coating with a WS2 dosage of 2.5 g/L in the bath exhibited excellent mechanical properties, with a hardness of 10.9 GPa, a friction coefficient of ~0.51, and a wear rate of 8.4 × 10−15 m3N−1×m−1 at room temperature, and maintained optimal performance at high temperatures. At operating temperatures of 200, 400, and 600 °C, the form of wear was adhesive wear for coatings with a WS2 dosage < 1.5 g/L and abrasive wear for coatings with a WS2 dosage ≥ 1.5 g/L. The synergism of WS2 and Si3N4 particles refined the grains of the Ni-P matrix in as-plated coatings and obviously reduced the friction coefficient of friction pairs in annealed coatings at all operating temperatures.

Electrodeposition and Tribological Properties of Self-Lubricating Sn-Ni-PTFE Composite Coating

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Preparation and Tribological Properties of the Carbon Nanotubes–ni–p Composite Coating

Tribological performance of Ni-W/PTFE composite coating via pulse electrodeposition

Electrochemical Preparation and Characterization of Ni–PTFE Composite Coatings from a Non-Aqueous Solution Without Additives

Friction and Wear Behavior of Electroless Wear-Resistant and Self-Lubricating Ni-P Composite Coatings

Preparation and properties of Ni-P/Bi self-lubricating composite coating on copper alloys

Research of electrodeposited RE-Ni-Fe-P-PTFE composite coating

Electroless Preparation and Tribological Properties of Ni-P-Carbon Nanotube Composite Coatings under Lubricated Condition

Friction and Wear Behavior of PTFE Coatings Modified with Poly (methyl Methacrylate)

Preparation and characterization of Ni-P-Al2O3-PTFE nanocomposite coatings by unidirectional jet electrodeposition

Corrosion and wear resistance behaviors of electroless Ni–Cu–P–TiN composite coating

Electrodeposition of Ni-P composite coatings: A review

Improvement of the Tribological Properties and Corrosion Resistance of Epoxy–PTFE Composite Coating by Nanoparticle Modification

Electrodeposition of RE-Ni-Fe-P-PTFE Composite Coating

Preparation and tribological properties of Ni-P electroless composite coating containing inorganic fullerene-like WS2 nanomaterials

High Temperature Tribological Behavior of Electroless Plating Ni-P-Si3N4-WS2 Composite Coatings

Tribological investigation into nickel-coated graphite polytetrafluoroethylene composites

Enhanced wear resistance of Ni-Mo-TiN composite coating by synergistic effect of tough Ni-Mo matrix and hard TiN particles

Characterization and Tribological Behavior of Electroless-Deposited Ni-P-PTFE Films on NBR Substrates for Dynamic Contact Applications

Tribological Behavior and Surface Analysis of Ni–P/BP Coatings