Abstract:Keto-hydrazide cross-linking chemistry between diacetone acrylamide (DAAM) and adipic acid dihydrazide (ADH) has been widely applied in conventional emulsion polymerization to render materials with specific chemical and physical properties. However, significant drawbacks are usually associated with the conventional process, such as the migration of low-molar-mass surfactants, and the low cross-linking efficiency due to the random distribution of the cross-linkers throughout the nanoparticles. We demonstrate here the concept of surface cross-linking of latexes in a RAFT-mediated surfactant-free procedure that overcomes the migration of surfactants while improving the cross-linking efficiency of latexes. Specifically, the “surface cross-linking” here refers to the cross-linking of colloidal particles’ surfaces during the film formation process. First, an amphiphilic RAFT agent with the incorporation of a cross-linking unit (DAAM) was designed and synthesized; the following controlled emulsion polymerizations provide a series of surfactant-free latexes with excellent colloidal stabilities, high solid contents (>40.0 wt %), and a size range of 150–250 nm. To access RAFT latexes with different cross-linking degrees and mechanisms, amphiphilic RAFT agents with different units of cross-linking component (DAAM) were designed and implemented for the controlled emulsion polymerization of styrene and n-butyl acrylate. Next, the surface cross-linkable and randomly cross-linkable RAFT latexes and corresponding films were prepared. It was found that the surface cross-linked films exhibited not only improved Young’s modulus and storage modulus but also better solvent resistance compared to the control group with DAAM units randomly distributed throughout the particle systems. Remarkably, it was noticed that the surface cross-linking process can simultaneously increase the strain at break and ultimate stress, and this is the first observation of such a phenomenon in DAAM/ADH cross-linked latex films. Overall, this study represents the first attempt that combines surfactant-free RAFT-mediated emulsion polymerization with the surface cross-linking chemistry to produce cohesive films with enhanced and tunable mechanical properties. This universal synthetic strategy is applicable to a broad range of commercial monomers and can be used as a platform technology for advanced industrial applications.

Novel Self‐crosslinking Film from Hydrogenated Carboxylated Nitrile Rubber Latex

Self-Cross-Linking Hydrogenated Nitrile-Butadiene Rubber Latex/Polyvinyl Chloride Emulsion Composite Film and Its Properties

Novel Cross‐Linked Films Prepared from Hyperbranched Poly(amine‐ester)

Polyvinyl Pyrrolidone Grafted Silica Reinforced Hydrogenated Carboxylated Nitrile Latex Film with Improved Mechanical Properties

Hydrogenation of Carboxyl Nitrile Butadiene Rubber Latex Using a Ruthenium-Based Catalyst

Novel self-cross-linking fluorinated polyacrylate latex films with short chain perfluoroalkyl group: Surface free energy and surface reorganization

HYDROGENATED BUTADIENE-ACRYLONITRILE-BUTYLACRYLATE RUBBER AND ITS PROPERTIES

A bio-based, self-healable, conductive rubber film with oxidized cellulose nanofiber segregated network

Study on preparing novel cross-linked and fluorinated acrylate latex

Synthesis and Characterization of Self-cross Linking Hybrid Silicone-acrylate Emulsion at Ambient Temperature

Iron (III) cross-linked thermoplastic nitrile butadiene elastomer with temperature-adaptable self-healing property

New Method for Hydrogenating Nbr Latex

Synthesis and characterization of crosslinkable latex with interpenetrating network structure based on polystyrene and polyacrylate

Self Film‐forming and Opaque Hollow Latexes Fabricated Via Seeded Emulsion Polymerization Followed by Alkali Post‐treatment

Preparation and Characterisation of Novel Cross-Linked Poly (IBOMA-BA-DFMA) Latex

Structure and Performance of Hydrogenated Natural Rubber Prepared by the Latex Method

Preparation and characterization of self-crosslinking acrylate emulsion modified by divinyl silane

Study on the structural and properties of composite films prepared by blending EUL and NBRL

Nanoparticle Surface Cross-Linking: A Universal Strategy to Enhance the Mechanical Properties of Latex Films

Low-crosslinking Multi-Functionalization HVBR Prepared in Solvent Free Process by Anionic Grafted Reaction

Carboxylated butadiene–styrene rubber/halloysite nanotube nanocomposites: Interfacial interaction and performance