Structure and Performance of Hydrogenated Natural Rubber Prepared by the Latex Method

Meiqin Ji,Dongmei Yue,Xiaohui Wu,Suhe Zhao,Shuquan Sun,Liqun Zhang
DOI: https://doi.org/10.1080/14658011.2017.1318500
2017-01-01
Plastics Rubber and Composites
Abstract:Hydrogenated natural rubber (HNR) with different degrees of hydrogenation was prepared by the latex method. The hydrazine hydrate/hydrogen peroxide/boric acid catalytic system could result in the hydrogenation of natural rubber (NR) under the latex state. The NR without hydrogenation contained around 13% of gel, when the hydrogenation degree reached 66.9%, the gel content was 34.4%. The decomposition temperature of HNR kept on increasing, which was all higher than that of NR and the glass transition temperature increased slightly. The cross-linking density of vulcanised rubber rose along with the increasing degree of hydrogenation, the NR cross-linking density was 0.114 mmol cm(-3), when the hydrogenation degree was 34.6%, 42.7% and 66.9%, the cross-linking density was 0.182, 185 and 221 mmol cm(-3), respectively. This further proved decreasing flexibility of the HNR after hydrogenation and weakening crystallisation of HNR along with increasing degree of hydrogenation.
What problem does this paper attempt to address?