Abstract:The tension-compression yield asymmetry caused by the strengthening of Mg-Zn-Gd-Zr alloy due to extrusion deformation is an important issue that must be addressed in its application. In this study, the effects of loading direction on the tensile and compressive mechanical behaviors of Mg-5Zn-2Gd-0.2Zr alloy were systematically investigated. As the loading angle (the angle between the loading direction and the extrusion direction) increases from 0° to 30°, 45°, 60° and 90°, the tensile yield strength decreases more significantly than the compressive yield strength. Consequently, the tension-compression yield asymmetry is gradually improved. Additionally, the ultimate compressive strength decreases more markedly than the ultimate tensile strength with the increment of the loading angle. In tensile tests conducted at 0°, 30° and 45°, two distinct stages of decreasing strain hardening rates are typically observed. For the 60° and 90° tensile tests, one unusual ascending stage of strain hardening rate is observed. For all compressive tests, three stages of strain hardening are consistently noted; however, the increment in strain hardening rate caused by {10–12} extension twinning decreases with the increasing loading angle. A model combining loading angle and Schmid factor distribution was established. The calculated results indicate that the dominant deformation modes during the yielding process also vary significantly with the loading conditions. This clarification highlights the differences in yield strength variations between tension and compression. Finally, an analysis of the plane trace and crack propagation direction near the fracture surface reveals the fracture mechanisms associated with tensile and compressive tests at different loading directions. This study promotes understanding of the mechanical behaviors of Mg-5Zn-2Gd-0.2Zr alloy under different loading directions, and helps to thoroughly elucidate the anisotropic effects of texture on the mechanical properties of magnesium alloys.

Tensile and Compressive Properties of Mg-3Al-2Zn-2Y Alloy at Different Strain Rates

Strain Rate Sensitivity and Adiabatic Shear Deformation of an Advanced Al-Mg Alloy

Mechanical properties and fracture behavior of Mg–3Al–1Zn alloy under high strain rate loading

Tension behavior of Ti–6.6Al–3.3Mo–1.8Zr–0.29Si alloy over a wide range of strain rates

Strain-Rate-Dependent Tensile Response of Ti–5Al–2.5Sn Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Hot deformation behavior of novel high-strength Mg-0.6Mn-0.5Al-0.5Zn-0.4Ca alloy

Tensile Mechanical Properties and Deformation Mechanism of the Extruded ZM61 Magnesium Alloy at High Strain Rates

Effect of Loading Direction on Tensile-Compressive Mechanical Behaviors of Mg-5Zn-2Gd-0.2Zr Alloy with Heterogeneous Grains

The Dynamic Recrystallization in a Hot Compressed Al‐Zn‐Mg‐Cu‐Sc‐Zr Alloy: the Role of Strain Rate

Effect of Strain Rate on the Tension Behavior of Ti–6.6Al–3.3Mo–1.8Zr–0.29Si Alloy at Low Temperatures

Strain Rate Effects on the Mechanical Properties of an AlCoCrFeNi High-Entropy Alloy

Strain Rate and Temperature Effects on Formability and Microstructure of AZ31B Magnesium Alloy Sheet

Effect of strain rate on the tension–compression asymmetric responses of Ti–6.6Al–3.3Mo–1.8Zr–0.29Si

High Strain-Rate Behavior and Deformation Mechanism of a Multi-Layer Composite Textured AZ31B Mg Alloy Plate

Strain Rate Sensitivity of Tensile Properties in Ti-6.6Al-3.3Mo-1.8Zr-0.29Si Alloy: Experiments and Constitutive Modeling

Temperature-Dependent Tension Plastic Deformation and Fracture Behavior of Ti-6.6Al-3.3Mo-1.8Zr-0.29Si Alloy at High Strain Rates

Effect of Strain Rate and Temperature on Dynamic Mechanical Behavior and Microstructure Evolution of Ultra-High Strength Aluminum Alloy

Effects of temperature and strain rate on the tension-compression asymmetric plastic deformation behavior of ME20M magnesium alloy: Experiments and modeling

Effect of strain rate on microstructure and mechanical properties of spray-formed Al–Cu–Mg alloy

Influence of nanoparticles on the compressive rate-sensitivity of magnesium alloys