Effect of cold deformation and annealing on intergranular corrosion property of 5E06 aluminium alloy plates

ZHANG Xin-ming,NIE Zuo-ren,HUANG Hui,WENG Sheng-ping,GAO Kun-yuan
DOI: https://doi.org/10.19476/j.ysxb.1004.0609.2013.11.006
2013-01-01
Abstract:The effects of cold deformation and annealing on the intergranular corrosion property of 5E06 aluminium alloy plates were investigated by intergranular corrosion property tests and transmission electron microscope (TEM). The results show that the intergranular corrosion property of 5E06 aluminium alloy plates has close relationship with the distribution, morphology and quantity ofβphase. When the cold deformation is under 40%,βphase is easy to precipitate continuously at grain boundaries which will worsen the intergranular corrosion property. When the cold deformation exceeds 55%,βphase is not easy to achieve succession after stabilizing annealing and the 5E06 aluminum alloy plates have favorable intergranular corrosion property. Sensitization tests indicate that the effect of stabilizing at 120℃is not desirable for 5E06 aluminum alloy plates at cold deformation of 55%-80%, whereas the aluminum alloy plates annealed at 220 ℃ can obtain homogeneous subgrains and β phase distributes discretely at grain boundaries and subgrain boundaries which can reduce the degree of supersaturation to some extent. Therefore, the intergranular corrosion property of 5E06 aluminum alloy plates at stabilizing annealing states won’t degenerate obviously in the long-term using process.
What problem does this paper attempt to address?