Abstract:The directional solidification experiment was carried out on ternary alloy of Al-3.46Cu-5.70Si (in wt.%) and an I-shaped variable cross-section ingot was obtained. The solidification structure, secondary dendrite arm spacing and macrosegregation at different positions of the ingot were investigated by scanning electron microscopy and component analysis. The results show that the grain size and the second dendrite arm space of the ingot increase with the increasing of the distance from the crystallizer to the position, because of the differences in solidification rate. Obviously macrosegregation of element Cu and Si was observed. Near the crystallizer of the ingot positive macrosegregation appears, and negative macrosegregation in vertical direction and positive macrosegregation in the lateral direction at the variable section position of ingot are observed. And the experiment results show that the degree of macrosegregation of Cu is larger than Si.

Investigation of Macrosegregation of Ternary Al-3.46Cu-5.70Si Alloy Casting with Variable Cross-Section in Directional Solidification