Abstract:A simple one-step process was developed to fabricate a super-hydrophobic surface on copper alloy substrates, which was applied by immersing the sheets in a solution containing sodium hydroxide (NaOH), ammonium persulphate ((NH4)(2)S2O8) and fluoroalkyl-silane (FAS-17) molecules. The consequent surface was characterized by contact angle measurements, scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The water contact angle (CA) and sliding angle (SA) on the resulting surface were similar to 158 degrees and similar to 4 degrees, respectively. Here, the stability of the obtained surfaces was measured by a wearing test. The damaged coatings can be quickly repaired by a one-step solution-immersion process. Subsequently, the liquid/solid friction on the distinct wetting surface was studied by using a water spraying system. By comparing the friction on a normal surface and the as-prepared surface at different flow velocities, we found that superhydrophobic coatings exhibited an excellent drag reduction of similar to 40% at a lowwall shear rate and similar to 20% at highwall shear rate. Based on these results, we attribute the superhydrophobic drag-reducing results to the plastron effect, which is characterized by surface wetting and roughness. This study not only presented a simple one-step method to fabricate a superhydrophobic surface on the copper alloy substrates but also showed the drag-reducing effect on the obtained surfaces for engineering applications.

One-step solution immersion process to fabricate superhydrophobic surfaces on light alloys.

Low-Cost One-Step Fabrication of Superhydrophobic Surface on Al Alloy

Fabrication of Superhydrophobic Aluminum Surface by Droplet Etching and Chemical Modification

Preparation of Stable Superamphiphobic Surfaces on Ti-6Al-4V Substrates by One-Step Anodization

Superhydrophobic Surfaces on Light Alloy Substrates Fabricated by a Versatile Process and Their Corrosion Protection

Bioinspired One Step Hydrothermal Fabricated Superhydrophobic Aluminum Alloy with Favorable Corrosion Resistance

Facile Fabrication of Superhydrophobic Surfaces with Low Roughness on Ti–6Al–4V Substrates Via Anodization

Superhydrophobic surfaces created by a one-step solution-immersion process and their drag-reduction effect on water

Fabrication of superhydrophobic surfaces on aluminum substrates via electrochemical etching and re-deposition

A Simple Immersion Approach for Fabricating Superhydrophobic Mg Alloy Surfaces

Fabrication of Superhydrophobic Micro-Nanostructured Aluminum Alloy Surface Via a Cost-Effective Processing Using an Ultra-Low Concentration of Fluoroalkylsilane

Fabrication and Characterization of Superhydrophobic Surfaces on Aluminum Alloy Substrates

A green one-step fabrication of superhydrophobic metallic surfaces of aluminum and zinc

Fabrication of Super-Hydrophobic Surfaces on Aluminum Alloy Substrates by RF-sputtered Polytetrafluoroethylene Coatings

Fabrication of Super-Hydrophobic Surface on Aluminum Alloy by A Simple Immersion Method

Wettability Transition of Metallic Surfaces from Laser-Generated Superhydrophilicity to Water-Induced Superhydrophobicity Via a Facile and Eco-Friendly Strategy

A simple strategy towards construction of fluorine-free superhydrophobic aluminum alloy surfaces: self-cleaning, anti-corrosion and anti-frost

A Novel Simple Approach to Preparation of Superhydrophobic Surfaces of Aluminum Alloys

Fabrication of Functional Surfaces of Aluminum Alloy with a Transition from Superhydrophilic to Superhydrophobic by Nanosecond Laser Irradiation

Fabrication of Superhydrophobic Surfaces on Mg Alloy Substrates Via Primary Cell Corrosion and Fluoroalkylsilane Modification

Fabrication of a Highly Stable Superhydrophobic Surface with Dual-Scale Structure and Its Antifrosting Properties