Microstructure and magnetic properties of Ni–Zn ferrite ceramics with different Ni2+ contents
Wei Li,Bo Dai,Zhao Li,Hongwei Yang,Guixiang Liu,Fang Xu
DOI: https://doi.org/10.1007/s10854-024-12101-w
2024-03-10
Journal of Materials Science Materials in Electronics
Abstract:A series of Ni x Zn 1− x Fe 2 O 4 ( NiZn, x = 0.15, 0.25, 0.35, 0.45, 0.65, 0.7, 0.8, 0.85) ferrites were prepared via a solid-phase sintering method. The microstructure, phase, and gyromagnetic properties of the NiZn samples were studied in depth. It was found that the lattice constants, density, and hardness of the samples gradually decreased with increasing Ni 2+ content. X-ray diffraction confirmed that all of the samples were in the spinel phase. Scanning electron microscopy indicated that the grain sizes were more uniformly distributed when x = 0.65. Raman analysis showed that the variation of Ni 2+ content affected the occupancy distribution of ferrite ions. The results indicated that Zn 2+ mainly occupied the A-site and that Ni 2+ mainly occupied the B-site. The coercivity ( H c ) of NiZn increased with increasing Ni 2+ content. Meanwhile, the saturation magnetization ( M s ) initially increased and then decreased. When x = 0.65, the total molecular magnetic moment started decreasing because of the decrease in the net A-site magnetic moment. The sample that had a composition of Ni 0.65 Zn 0.35 Fe 2 O 4 had the highest M s intensity with a value of 78.68 emu/g and a maximum value of 4 πM s = 4780 Gs.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied