Preparation and Characterization of Nano-Powder Zirconia Stabilized by Magnesia

SHAN Ke,GUO Xing-min

DOI: https://doi.org/10.3969/j.issn.1673-0224.2013.03.020

2013-01-01

Abstract:Nano-powder magnesia stabilized zirconia Zr1?xMgxO2?x powders were prepared by sol-gel process using oxalic acid as precipitant. The crystal phase composition and structure of oxide powders were determined by X-ray diffraction (XRD) and field emission scanning electron microscope (FESEM), respectively. The results of XRD show that tetragonal phase ZrO2 and little monoclinic phase ZrO2 form at 550 ℃, while the tetragonal Zr1?xMgxO2?x forms at 350 ℃. When x is below 0.08 and with temperature increasing, part of t-ZrO2 transforms to m-ZrO2 , and the ratio of transformtion decreases with increasing x value, when x is above 0.10, t-ZrO2 transformation ratio increases with increasing temperature. The generation of oxygen defect after Mg2+ replacing Zr4+ is the main factor to influence the stabilization of the ZrO2 crystal structure. The crystillize size of t-ZrO2 increases from 42 nm to 100 nm when temperature increases from 350 ℃ to 650 ℃, and t-ZrO2 crystillize size decreases from 110 nm to 97.8 nm with MgO-doped amount increases from 0.04 to 0.10. Nano grain size is favorable for the stability of t-ZrO2.