Akun Liang,Israel Osmond,Georg Krach,Lan‐Ting Shi,Lukas Brüning,Umbertoluca Ranieri,James Spender,Ferenc Tasnadi,Bernhard Massani,Callum R. Stevens,Ryan Stewart McWilliams,Eleanor Lawrence Bright,Nico Giordano,Samuel Gallego‐Parra,Yuqing Yin,Andrey Aslandukov,Fariia Iasmin Akbar,Eugene Gregoryanz,Andrew Huxley,Miriam Peña‐Alvarez,Jian‐Guo Si,Wolfgang Schnick,Maxim Bykov,Florian Trybel,Dominique Laniel

Abstract:Two recoverable tungsten nitrides, namely W2N3 and W3N5, are synthesized using laser‐heated diamond anvil cells. Both compounds exhibit a high bulk modulus, hardness, and superconducting transition temperature. Transition metal nitrides, particularly those of 5d metals, are known for their outstanding properties, often relevant for industrial applications. Among these metal elements, tungsten is especially attractive given its low cost. In this high‐pressure investigation of the W–N system, two novel ultra‐incompressible tungsten nitride superconductors, namely W2N3 and W3N5, are successfully synthesized at 35 and 56 GPa, respectively, through a direct reaction between N2 and W in laser‐heated diamond anvil cells. Their crystal structure is determined using synchrotron single‐crystal X‐ray diffraction. While the W2N3 solid's sole constituting nitrogen species are N3‐ units, W3N5 features both discrete N3‐ as well as N24‐ pernitride anions. The bulk modulus of W2N3 and W3N5 is experimentally determined to be 380(3) and 406(7) GPa, and their ultra‐incompressible behavior is rationalized by their constituting WN7 polyhedra and their linkages. Importantly, both W2N3 and W3N5 are recoverable to ambient conditions and stable in air. Density functional theory calculations reveal W2N3 and W3N5 to have a Vickers hardness of 30 and 34 GPa, and superconducting transition temperatures at ambient pressure (50 GPa) of 11.6 K (9.8 K) and 9.4 K (7.2 K), respectively. Additionally, transport measurements performed at 50 GPa on W2N3 corroborate with the calculations.

Nanocrystalline Tungsten Hydrides At High Pressures

Compressibility And Strength Of Nanocrystalline Tungsten Boride Under Compression To 60gpa

High-pressure Preparation of Bulk Tungsten Material with Near-Full Densification and High Fracture Toughness

Synthesis of Nano-Polycrystalline Diamond under High Pressure and High Temperature

Nano-polycrystalline diamond formation under ultra-high pressure

The Hydrogen‐bond Effect on the High Pressure Behavior of Hydrazinium Monochloride

Synthesis Of New Nickel Hydrides At High Pressure

Synthesis of Na 3 WH 9 and Na 3 ReH 8 Ternary Hydrides at High Pressures

Microstructures and properties of nanocrystalline W-based alloys produced by resistance sintering under ultrahigh pressure

Synthesis of Na3WH9 and Na3ReH8 Ternary Hydrides at High Pressures

Synthesis of Ni 2 H 3 at High Temperatures and Pressures

Binderless nanocrystalline tungsten carbide with enhanced hardness induced by high-pressure sintering

Synthesis of technetium hydride TcH$_{1.3}$ at 27 GPa

High‐Pressure Synthesis of Ultra‐Incompressible, Hard and Superconducting Tungsten Nitrides

Synthesis, Crystal Structure, and Elastic Properties of Novel Tungsten Nitrides

Synthesis and stability of tantalum hydride at high pressures

Pressure-Induced Phase Transition and Compression Properties of HfO 2 Nanocrystals

Growth and Annealing Study of Hydrogen-Doped Single Diamond Crystals under High Pressure and High Temperature

Synthesis, Phase Evolutions, and Stabilities of Boron-Rich Tungsten Borides at High Pressure.

Pressure-Induced Phase Transition and Compression Properties of HfO2 Nanocrystals.

Experimental Study of Crystal Structure and Superconductivity in Hydrides under High Pressure