Abstract:While most of the rare earth metals readily form trihydrides, due to increased stability of the filled 4f electronic shell for Yb(II), only YbH$_{2.67}$, formally corresponding to Yb$^{\rm II}$(Yb$^{\rm III}$H$_4$)$_2$ or Yb$_3$H$_8$, remains the highest hydride of ytterbium. Utilizing diamond anvil cell methodology and synchrotron powder x-ray diffraction we have attempted to push this limit further via hydrogenation of metallic Yb (at room temperature and heated in situ) and of Yb$_3$H$_8$. Compression of the latter has also been investigated in a neutral pressure transmitting medium, PTM. While the in situ heating of Yb facilitates the formation of YbH$_2$ plus x hydride, we have not observed the clear qualitative differences between the systems compressed in H$_2$ and He or Ne PTM. In all these cases a sequence of phase transitions from the unit cells of P-31m symmetry to the I4/m and I4/mmm systems occurred within ca. 13 to 18 GPa and around 27 GPa, respectively. At the same time, the molecular volume of the systems compressed in H$_2$ PTM is ca. 1.5% larger than of those compressed in inert gases, suggesting a small hydrogen uptake. Nevertheless, hydrogenation towards YbH$_3$ is incomplete, and polyhydrides do not form up to the highest pressure studied here of ca. 75 GPa. As pointed out by our electronic transport measurements under compression in NaCl PTM, the mixed-valence Yb$_3$H$_8$ retains its semiconducting character up to at least 50 GPa, although the very low remnant activation energy of conduction, smaller than 5 meV, suggests that the metallization under further compression should be achievable. Finally, we provide a theoretical description of a hypothetical stoichiometric YbH$_3$.

Synthesis of technetium hydride TcH$_{1.3}$ at 27 GPa

Synthesis and stability of tantalum hydride at high pressures

Ternary superconducting hydrides stabilized via Th and Ce elements at mild pressures

Synthesis, structure and electric conductivity of higher hydrides of ytterbium at high pressure

Superconductivity up to 243 K in yttrium hydrides under high pressure

Nanocrystalline Tungsten Hydrides At High Pressures

Designing ternary superconducting hydrides with A15-type structure at moderate pressures

Synthesis, Structure, and Electric Conductivity of Higher Hydrides of Ytterbium at High Pressure

Prediction of high-Tc superconductivity in ternary actinium beryllium hydrides at low pressure

Synthesis of clathrate cerium superhydride CeH9 below 100 GPa with atomic hydrogen sublattice

Design of superconducting compounds at lower pressure via intercalating XH molecules (X = B, C, and N) into fcc lattices

Discovery of superconductivity in technetium-borides at moderate pressures

Designing Quaternary Hydrides with Potential High T$_c$ Superconductivity

Superconductivity at 215 K in lanthanum hydride at high pressures

Enhancement of the superconducting critical temperature realized in the La-Ce-H system at moderate pressures

High-Pressure Synthesis of Seven Lanthanum Hydrides with a Significant Variability of Hydrogen Content

High-Temperature Superconductivity in the Ti--H System at High Pressures

Superconductivity at ~70 K in Tin Hydride SnHx under High Pressure

Novel Superconducting Ternary Hydrides under High Pressure

Synthesis of clathrate cerium superhydride CeH9 at 80-100 GPa with atomic hydrogen sublattice

Pressure-Induced superconductivity in tantalum superhydrides