Controlled Synthesis of Long-Wavelength Multicolor-Emitting Carbon Dots for Highly Efficient Tandem Luminescent Solar Concentrators
Jun Wang,Jianying Wang,You Xu,Junjun Jin,Wenxin Xiao,Di Tan,Jinhua Li,Tao Mei,Longjian Xue,Xianbao Wang
DOI: https://doi.org/10.1021/acsaem.0c02265
IF: 6.4
2020-11-23
ACS Applied Energy Materials
Abstract:Long-wavelength multicolor emission and high photoluminescence quantum yields (PLQYs) play a key role in carbon dot (CD)-based luminescent solar concentrators (LSCs). Herein, long-wavelength multicolor-emitting CDs with high PLQYs had been synthesized by one-step solvothermal process of phenylenediamine (PD) isomers (<i>m</i>-, <i>o</i>-, <i>p</i>-PDs) in the presence of lignin. Relying on the introduction of lignin, green (G), yellow (Y), and red (R) emissive CDs without excitation wavelength dependence could be achieved. The R, Y, G CDs showed clearly red shift effect in PL emission spectra, compared to the control CDs samples (Rc, Yc, Gc CDs) only based on PD isomers as precursors. The PL red shift probably resulted from the size effect of CDs. Remarkably, the R, Y, G CDs with high PLQYs (15.01, 41.52, and 7.60%) had been achieved owing to their long PL lifetimes, which is also higher than that of control Rc, Yc, Gc CDs samples (PLQYs of 12.66, 38.32, and 3.48%). Moreover, the tandem LSCs based on the R, Y, G CDs had further been demonstrated. The external optical efficiency (η<sub>opt</sub>) and power conversion efficiency (η) of LSCs had been enhanced greatly up to 4.03 and 2.92%, respectively, compared to that of LSCs based on the control CDs LSCs (only have 3.76 and 2.66%).The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.0c02265?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.0c02265</a>.Chemical reagents; synthesis of the R, Y, G-CDs and the Rc, Yc, Gc-CDs; preparation of CD-based LSCs with various thicknesses; characterization. Experimental parameters and calculations; HRTEM and AFM images of Rc-CDs, Yc-CDs, Gc-CDs; high-resolution XPS spectra of CDs; FTIR spectra of CDs; (Figure S4) surface wettability of R-CDs; surface wettability of Y-CDs; surface wettability of G-CDs; PL stability spectra of CDs; excitation-independence of PL spectra of CDs; fitted PL decay spectra for CDs; SEM images of Y CD-based LSCs with different thicknesses; absorption spectra of LSCs; photographs of tandem LSCs under daylight and UV light and emission spectra of the Rc, Yc, Gc CD-based tandem LSCs; overview and comparison of literature results for CD-based LSCs; performances of CD-based LSCs at the initial state and after 7 days; relationship of the photocurrent density and photovoltage (<i>J</i>–<i>V</i>) of the single layer (R, Y, G) and tandem LSCs (5 × 5 × 0.1 cm<sup>3</sup>); lifetime data of CDs under 420 nm excitation; PLQY value of CDs under 420 nm excitation; PV parameters of various CD-based LSCs (0.32 wt % of CD concentration and a thickness of 9.60 μm); PV parameters of various CD-based LSCs after 7 days; overviews of literature results for CD-based LSCs; and PV parameters of the single layer (R, Y, G) and tandem LSCs (5 × 5 × 0.1 cm<sup>3</sup>) (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.0c02265/suppl_file/ae0c02265_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels