Structure stability of organic montmorillonite used for preparing polyethylene/montmorillonite nanocomposite
H. Yang,Q. Zheng
DOI: https://doi.org/10.1023/A:1025715514900
2003-01-01
Journal of Materials Science Letters
Abstract:As a novel kind of composite, polymer/montmorillonite nanocomposites have attracted more and more researcher’s attention due to their far-reaching academic and application significance. Because of its special structure, the montmorillonite (MMT), especially the organically modified montmorillonite or organic montmorillonite (org-MMT), has been widely used for preparing polymer/montmorillonite nanocomposite by means of intercalated polymerization [1‐4], solution intercalation [5‐7] and melt intercalation [8‐11]. For generating polymer-layered silicate nanocomposite, melt intercalation is more efficient and environmentallybenign as compared with the other two intercalation processes, and can be processed with general plastics processing equipment such as extruders. Generally, org-MMT with a polymer matrix must be processed under heat and force during melt intercalation. However the layer stacking of org-MMT structure is unstable upon heating [12] since the organically modified agents which is inserted into the spaces between the MMT layers will decompose under circumstance of heat or strong force. In this paper, we paid our attentions to the structure stability of organic montmorillonite modified by cetyltrimethylammonium bromide and its mixtures with stearic acid through ball mill. “Kunipia F”(sodium montmorillonite (MMT), cation exchange capacity = 115 meq/100 g, purity ≥99%, Kunimine Ind. Co. Japan), CTAB (cetyltrimethylammonium bromide, analytically pure, Shanghai Chem. Reagent Co., China), low density polyethylene (LDPE) (melt flow rate = 7.6 g/10 min at 190 ◦ C, 2.16 kg, Beijing Yanshan Petrochem. Co. Ltd., China), ethylene vinyl acetate copolymer (EVA) (H2020, Polyolefin Co. Singapore) and commercially available stearic acid (HSt) were used here, as modifiers, matrix of composites and compatiblizer, etc. respectively. Organic montmorillonite (org-MMT) was prepared from MMT by ion exchange reaction using CTAB in water according to the reported method [13]. Org-MMT, org-MMT/HSt(10/1) and org-MMT/HSt(5/1) were ball milled for different times with sixteen small balls (� = 10 mm) and two big balls (� = 20 mm) under a constant mill speed (150 rpm) respectively. The thermal stability of org-MMt was evaluated using thermogravimetry (TG). LDPE/EVA /org-MMT (85/12/3) were blended in a twin-screw extruder (TSE 16 TC, ∗ Author to whom all correspondence should be addressed. PRISM, UK). The measurements of dynamic viscoelasticity were conducted by Advanced Rheology Expansion System (ARES, Rheometrics Sci. Ltd., USA) using parallel model with diameter of 25 mm. The changes of sample structure were characterized by X-ray diffraction (XRD). The space between the two layers of MMT is given by the following expressions d = λ