abrication of a superhydrophobic surface from porous polymer using hase separation
Jianfeng Liu,Xinyan Xiao,Yinlong Shi,Caixia Wan
2014-01-01
Abstract:The present work reports a simple method to fabricate superhydrophobic porous polymeric surfaces by a phase separation process. The method involves the in situ polymerization of butyl methacrylate (BMA) and ethylene dimethacrylate (EDMA) in the presence of co-porogens of 1,4-butanediol (BDO) and N-methyl-2-pyrrolidone (NMP) to afford superhydrophobic surfaces with the micro/nano roughness structure. The influences of the polymerization mixture on the morphology and hydrophobicity were investigated by adjusting the composition of the co-porogens and the mass ratio of monomers to com .co uperhydrophobic orous polymer orogen hase separation ater contact angle porogens, respectively. And a precise description of the underlying mechanism of the microstructure formation was presented. The as-prepared surface shows a superhydrophobicity with water contact angle (WCA) of 159.5◦ and low sliding angle (SA) of 3.1◦. Moreover, the superhydrophobic surface shows good chemical stability with better resistance to acid, alkali or salt aqueous solutions and excellent thermal stability. The method is simple and low-cost and can be used for the preparation of the self-cleaning superhydrophobic surfaces. © 2014 Elsevier B.V. All rights reserved. ww w. sp . Introduction Superhydrophobic surfaces with water contact angle (WCA) arger than 150◦ and sliding angle (SA) lower than 10◦ have ttracted considerable interest during the last years [1–5]. Their ossible industrial and practical applications range from selfleaning coatings, oil–water separation, and micro-fluidics to ater-proof textiles [6–8]. In nature, many plants and animals xhibit superhydrophobic property, such as lotus leaves, rice eaves, red rose petals, gecko feet and desert beetle, and so on. he investigation of lotus leaves demonstrated that the combinaion of multi-scaled rough structure and the low surface energy ompound is essential for superhydrophobicity [9]. In order to imic the superhydrophobic effect, many approaches, such as ol–gel method [10], template method [11], solution immersion rocess [12,13], electrospinning [14], phase separation [15–19], olymer/nanoparticle composite [20] and laser method [21], have een developed. Among all these methods phase separation is a Abbreviations: BMA, butyl methacrylate; EDMA, ethylene dimethacrylate; BDO, ,4-butanediol; NMP, N-methyl-2-pyrrolidone; AIBN, 2,2′-azobisisobutyronitrille; CA, water contact angle; SEM, scanning electron microscope; AFM, atomic force icroscopy. ∗ Corresponding author. Tel.: +86 20 87112074. E-mail address: cexyxiao@scut.edu.cn (X. Xiao). 169-4332/$ – see front matter © 2014 Elsevier B.V. All rights reserved. ttp://dx.doi.org/10.1016/j.apsusc.2014.01.053 relatively facile, efficient, and low cost method to attain superhydrophobic surface. Aruna et al. [22] prepared polystyrene (PS) based superhydrophobic films by non-solvent induced phase separation method using tetrahydrofuran (THF) as the solvent and different alcohols as non-solvents. And the prepared coatings exhibited a maximum WCA of 159◦. Pi et al. [23] prepared a polylactic acid (PLA) superhydrophobic film, in which a microphase separation happened during the film drying and the polyethylene oxide (PEO) formed microdomains for the dissimilarity of PLA and PEO. Finally, a porous and rough PLA film formed. Wei et al. [24] synthesized copolymers of styrene and 2,2,3,4,4,4-hexafluorobutyl methacrylate by bulk polymerization firstly. The copolymer was dissolved in THF, and then added ethanol into the solution thereafter, to induce phase separation. The WCA and SA were measured as 154.3◦and 5.8◦, respectively. The microstructures of the polymer films were controlled by the degree of phase separation. However, some limits are associated with these methods, such as specific humidity, suitable solvent and non-solvent, or low surface energy compound. The stability of the surface hydrophobicity is also a great problem. In this study, a facile phase separation process to fabricate superhydrophobic polymeric surfaces is reported. The process involves in situ polymerization of monomers in the presence of co-porogens. The co-porogens in the polymerization mixture lead to phase separation when the growing cross-linked polymer chains achieve a critical length. In order to minimize the surface energy, the precipitates of the polymer chains will reunite into conglomerations,