Evolutions of Microstructure and Mechanical Properties in Mg–5Li–1Zn–0.5Ag–0.5Zr–xGd Alloy
Bing-Yu Qian,Rui-Zhi Wu,Jian-Feng Sun,Jing-Huai Zhang,Le-Gan Hou,Xiao-Chun Ma,Jia-Hao Wang,Hai-Ting Hu
DOI: https://doi.org/10.1007/s40195-022-01509-0
2023-01-07
Acta Metallurgica Sinica (English Letters)
Abstract:The evolution of the microstructure and mechanical properties of alloy system with nominally composition Mg–5Li–1Zn–0.5Ag–0.5Zr– x Gd ( x = 0, 1.2, 2.4, 3.6, 4.8, 6) is evaluated based on computational phase diagram and corresponding experimental studies. The results show that grains are significantly refined with the increase of Gd content. The main phases of as-cast alloys are α -Mg, β -Li, AgLi 2 Mg, and Mg 3 Gd. With the increase of Gd content, the amounts of Mg 3 Gd phase and β -Li phase have been increased. When the Gd content exceeds 3.6 wt%, Mg 3 Gd phase precipitates in a form of the network at the grain boundaries. The precipitation of β -Li can be attributed to the competitive dissolution of Zn, Gd, and Li in Mg. Meanwhile, γ ′′ is formed after the addition of Gd, which grows and transforms into γ ′ with the increase of Gd content. In solidification process, stacking faults are formed by solid transformation of partial α -Mg and Mg 3 Gd. Eventually, with the synergistic effect of Mg 3 Gd, β -Li, and γ ′′ (or γ ′), as the Gd content increasing, the tensile strength of the alloy first increases, then decreases, and the elongation decreases. When the content of Gd is 4.8 wt%, the ultimate tensile strength and yield strength reach the maximum values of 227 MPa and 139 MPa, and the elongation is 18.1%, respectively.