Abstract:In this study, three types of three-layer functionally graded materials (FGMs) were designed by mainting the average content of the reinforcement constant and changing the span of the composition. The B 4 C particle-reinforced Al-matrix FGMs and a homogeneous composite (HC) with the same average composition were prepared using the laser additive manufacturing technique. The FGMs had a higher average secondary-phase content and grain size than the HC. Large (black) and reticulated (white) secondary phases corresponding to B 4 C phase, T phase, and MgZn 2 were observed in the as-deposited FGM samples. The content of the secondary phase in the middle layer was generally low. The bottom layer, which was in direct contact with the substrate, exhibited the smallest grain size. The hardness and wear resistance significantly improved owing to the high B 4 C content in the top layer. The flexural behaviors of each layer of the FGM in different directions were systematically studied. The plasticity of the single-layer material decreased with increase in the B 4 C content. When the bottom layer had a high B 4 C content, the flexural ability significantly reduced. Among all the samples, G2 with 8% B 4 C particle content in the top layer exhibited the best comprehensive mechanical properties. The hardness value, wear rate of the top layer, maximum bending stress, and maximum bending strain of the FGM were 177.5 HV, 0.367 × 10 −3 mm 3 /(N·m), 585.6 MPa, and 7.36%, respectively. This study can provide a reference value for the future design and development of wear-resistant gradient materials for aerospace applications.

Design and fabrication of laminated-graded zirconia self-lubricating composites

Design And Preparation Of High-Performance Alumina Functional Graded Self-Lubricated Ceramic Composites

High-Performance Self-Lubricating Ceramic Composites With Laminated-Graded Structure

Structure and Properties of Particles/rubber Composites Applied on Functionally Graded Lapping and Polishing Plate

Surface Engineering Design of Al2O3/Mo Self-Lubricating Structural Ceramics - Part II: Continuous Lubrication Effects of a Three-Dimensional Lubricating Layer at Temperatures from 25 to 800 °C

Influence of Structural Parameters and Compositions on the Tribological Properties of Alumina/graphite Laminated Composites

Microstructure and tribological properties of ZrO2(Y2O3) matrix composites doped with different solid lubricants from room temperature to 800°C

Tribological Behavior and Lubrication Mechanism of Self-Lubricating Ceramic/Metal Composites: the Effect of Matrix Type on the Friction and Wear Properties

Integrated preparation and enhanced performance of high-melting-point ZrC–Mo multilayer graded materials

Tribological Properties of Al2O3/Graphite-Al2O3 Laminated Composites under Water Lubrication Conditions

Fabrication and properties of machinable Al2O3/LaPO4 composites and FGMs

High-temperature self-lubricated properties of Al2O3/Mo laminated composites

Surface 3-D Lubrication Structure Design of Al2O3/Ni-laminated Ceramics to Improve Tribological Properties under Combined Environments

Fabrication of ZrO2/Mo-Si/Ni Functionally Graded Material by Dip-Coating

Surface Engineering Design of Alumina/Molybdenum Fibrous Monolithic Ceramic to Achieve Excellent Lubrication in a High Vacuum Environment

Composition design and mechanical properties of B 4 C/Al-Zn-Mg-Cu functionally graded materials prepared by laser additive manufacturing

Microstructure and Mechanical Properties of ZrO2/NiCr Functionally Graded Materials

Graded Machinable Si3N4/h-BN and Al2O3/LaPO4 Ceramic Composites

Surface Engineering Design of Alumina/Molybdenum Fibrous Monolithic Ceramic to Achieve Continuous Lubrication from Room Temperature to 800 °C

Fabrication and Tribological Behavior of Al2O3/MoS2–BaSO4 Laminated Composites Doped with in Situ Formed BaMoO4

Study on Controllable Tribological Behaviors of Self-Lubricating Laminated Composites