Abstract:As one of the most important surface strengthening method, shot peening is widely used to improve the fatigue and stress corrosion crack resistance of components by introducing the refined microstructure and compressive residual stress in the surface layer. However, the mechanical properties of this thin layer are different from the base metal and are difficult to be characterized by conventional techniques. In this work, a micro uniaxial tensile tester equipped with in-situ X-ray stress analyzer was employed to make it achievable on a nickel-aluminum bronze with shot peening treatment. According to the equivalent stress-strain relationship based on Von Mises stress criterion, the Young's modulus and yield strength of the peened layer were calculated. The results showed that the Young's modulus was the same as the bulk material, and the yield strength corresponding to the permanent plastic strain of 0.2% was increased by 21% after SP. But the fractographic analysis showed that the fracture feature of the surface layer was likely to transform from the dimple to the cleavage, indicating the improved strength might be attained at the expense of ductility. The monotonic and cyclic loading were also performed via the same combined setup. In addition, the specific relaxation behavior of compressive residual stress was quantified by linear logarithm relationship between residual stress and cycle numbers. It was found that the compressive residual stress mainly relaxed in the first few cycles, and then reached steady state with further cycles. The relaxation rate and the stable value were chiefly depended on the stress amplitude and number of cycles. The retained residual stress kept in compressive under all given applied stress levels, suggesting that the shot peening could introduce a more stable surface layer of compressive residual stress other than the elevated strength of nickel-aluminum bronze alloy. (C) 2017 Elsevier B.V. All rights reserved.

Surface layer investigation of duplex stainless steel S32205 after stress peening utilizing X-ray diffraction

Effect of Shot Peening on the Residual Stress and Microstructure of Duplex Stainless Steel

Surface Layer Characteristics of SAF2507 Duplex Stainless Steel Treated by Stress Shot Peening

Surface Layer Investigation of a Shot-Peened Duplex Stainless Steel Utilizing X-ray Diffraction

Determination of surface mechanical property and residual stress stability for shot-peened SAF2507 duplex stainless steel by in situ X-ray diffraction stress analysis

Effect of Prestress State on Surface Layer Characteristic of S30432 Austenitic Stainless Steel in Shot Peening Process

Evaluation of the Residual Stress and Microstructure Character in SAF 2507 Duplex Stainless Steel after Multiple Shot Peening Process

Uniformity of residual stress distribution on the surface of S30432 austenitic stainless steel by different shot peening processes

Effect of Stress Peening on Surface Layer Characteristics of (tib + TiC)/Ti–6Al–4V Composite

Experimental Study on Macro- and Microstress State, Microstructural Evolution of Austenitic and Ferritic Steel Processed by Shot Peening

Residual Stress Relaxation of Shot-Peened Deformation Surface Layer on Duplex Stainless Steel under Applied Loading

Surface mechanical properties of S30432 austenitic steel after shot peening

The influence of shot peening process on the residual stress and microstructure in deformed surface layer of S30432 austenitic stainless steel

Investigation on the Thermostability of Residual Stress and Microstructure in Shot Peened SAF 2507 Duplex Stainless Steel

Investigation on Surface Layers Characteristics of Pre-Stressed Shot Peening Inconel 625

The Effect of Multiple Shot Peening on the Corrosion Behavior of Duplex Stainless Steel

Effect of Ultrasonic Shot Peening on Stress Corrosion of 304 Austenitic Stainless Steel

Microstructure Thermostability of Shot Peened Duplex Stainless Steel Surface Layer

INVESTIGATION OF SURFACE GRADIENT MICROSTRUCTURE OF SHOT PEENED S30432 STEEL BY X-RAY LINE PROFILE ANALYSIS METHOD

Effect of Shot Peening on Residual Stress and Microstructure in the Deformed Layer of Inconel 625

Surface Mechanical Property and Residual Stress of Peened Nickel-Aluminum Bronze Determined by In-Situ X-Ray Diffraction