Abstract:In this study, shot peening (SP) treatment was implemented on a duplex (austenite and ferrite) stainless steel. By using X-ray diffraction residual stress determination and line profile analysis, the residual stress (including macro- and microstress) and microstructure evolutions in the surface layer of the shot peened material were discussed. Results pointed out that the initial thermal stress state were compressive (-80 MPa) in alpha phase and tensile (90 MPa) in gamma phase owing to the different thermal expansion coefficients of the two phases. After SP, the nonreversible plastic deformation of the surface layer and the interior of bulk was the main cause of the macrostresses. SP introduced more compressive residual stress into the gamma phase, the maximum compressive stress in gamma phase was similar to 1.3 times larger than that in alpha phase (-912 vs. -717 MPa) and occurred deeper in the sample interior (similar to 75 vs. 10 mu m). The inhomogeneous partitioning of the plastic strains, which was ascribed to the difference of the relative strength and deformation mechanism between the phases, was the contributing cause of microstresses. The average microstresses in surface layer of shot peened alloy were tensile in alpha phase and compressive in gamma phase, the magnitude of which changed with depth since the phase-specific plastic deformation was also a function of depth. The quantitatively microstructural analysis indicated that more deformation was stored in the gamma phase, the microstrain and dislocation density at the surface in gamma phase were about four and 2.6 times larger than that in alpha phase (7.25 vs. 1.83 x 10(-3), 3.9 vs. 1.5 x 10(15) m(-2)), respectively. Microhardness measurements showed that SP-induced work hardening was more evident in austenite, the hardness of austenitic phase was found significantly higher than that of ferritic phase in near surface region.

Effect of Prestress State on Surface Layer Characteristic of S30432 Austenitic Stainless Steel in Shot Peening Process

The influence of shot peening process on the residual stress and microstructure in deformed surface layer of S30432 austenitic stainless steel

Experimental Study on Macro- and Microstress State, Microstructural Evolution of Austenitic and Ferritic Steel Processed by Shot Peening

Surface mechanical properties of S30432 austenitic steel after shot peening

Uniformity of residual stress distribution on the surface of S30432 austenitic stainless steel by different shot peening processes

The evolution of residual stress and microstructure in shot peened s30432 austenitic stainless steel at high temperatures

Effect of surface shot peening on microstructure and properties of Super304H austenitic heat-resistant steels

Characterization of Surface Modification of 347 Stainless Steel Upon Shot Peening

Effect of Ultrasonic Shot Peening on Stress Corrosion of 304 Austenitic Stainless Steel

Surface Layer Characteristics of SAF2507 Duplex Stainless Steel Treated by Stress Shot Peening

Effect of Shot Peening on the Residual Stress and Microstructure of Duplex Stainless Steel

Surface layer investigation of duplex stainless steel S32205 after stress peening utilizing X-ray diffraction

Effect of Shot Peening on Residual Stress and Microstructure in the Deformed Layer of Inconel 625

Residual Stress Relaxation of Shot Peened Deformation Surface Layer on S30432 Austenite Steel under Applied Loading

Surface Modification of 304 Steel Using Triple-Step Shot Peening

Evaluation of the Residual Stress and Microstructure Character in SAF 2507 Duplex Stainless Steel after Multiple Shot Peening Process

Influence of shot peening on surface integrity of steel H13

Effect of Micro-Shot Peening on the Fatigue Performance of AISI 304 Stainless Steel

Investigation on Surface Layers Characteristics of Pre-Stressed Shot Peening Inconel 625

Effect of shot peening on the microstructure of laser hardened 17-4PH

Effect of Stress Peening on Surface Layer Characteristics of (tib + TiC)/Ti–6Al–4V Composite