Abstract:This research investigates the accelerated hydrolytic degradation process of both anatomically designed bone scaffolds with a pore size gradient and a rectangular shape (biomimetically designed scaffolds or bone bricks). The effect of material composition is investigated considering poly-ε-caprolactone (PCL) as the main scaffold material, reinforced with ceramics such as hydroxyapatite (HA), β-tricalcium phosphate (TCP) and bioglass at a concentration of 20 wt%. In the case of rectangular scaffolds, the effect of pore size (200 μm, 300 μm and 500 μm) is also investigated. The degradation process (accelerated degradation) was investigated during a period of 5 days in a sodium hydroxide (NaOH) medium. Degraded bone bricks and rectangular scaffolds were measured each day to evaluate the weight loss of the samples, which were also morphologically, thermally, chemically and mechanically assessed. The results show that the PCL/bioglass bone brick scaffolds exhibited faster degradation kinetics in comparison with the PCL, PCL/HA and PCL/TCP bone bricks. Furthermore, the degradation kinetics of rectangular scaffolds increased by increasing the pore size from 500 μm to 200 μm. The results also indicate that, for the same material composition, bone bricks degrade slower compared with rectangular scaffolds. The scanning electron microscopy (SEM) images show that the degradation process was faster on the external regions of the bone brick scaffolds (600 μm pore size) compared with the internal regions (200 μm pore size). The thermal gravimetric analysis (TGA) results show that the ceramic concentration remained constant throughout the degradation process, while differential scanning calorimetry (DSC) results show that all scaffolds exhibited a reduction in crystallinity (Xc), enthalpy (Δm) and melting temperature (Tm) throughout the degradation process, while the glass transition temperature (Tg) slightly increased. Finally, the compression results show that the mechanical properties decreased during the degradation process, with PCL/bioglass bone bricks and rectangular scaffolds presenting higher mechanical properties with the same design in comparison with the other materials.

Effect of Porosity on Long-Term Degradation of Poly (Ε-Caprolactone) Scaffolds and Their Cellular Response

Effect of Nonaffine Displacement on the Mechanical Performance of Degraded PCL and Its Graphene Composites: an Atomistic Investigation

Effects of Porosity and Pore Size on in Vitro Degradation of Three-Dimensional Porous Poly(d,l-Lactide-co-glycolide) Scaffolds for Tissue Engineering.

Degradation and Characterisation of Electrospun Polycaprolactone (PCL) and Poly(lactic-co-glycolic acid) (PLGA) Scaffolds for Vascular Tissue Engineering

Accelerated Degradation of Poly-ε-caprolactone Composite Scaffolds for Large Bone Defects

In Vitro and in Vivo Degradability and Cytocompatibility of Poly(l-Lactic Acid) Scaffold Fabricated by a Gelatin Particle Leaching Method

In vitro and in vivo degradability and cytocompatibility of poly(l-lactic acid) scaffold fabricated by a gelatin particle leaching method.

Effects of Degradation Media of Polyester Porous Scaffolds on Viability and Osteogenic Differentiation of Mesenchymal Stem Cells

Poly(l,l-lactide-co-glycolide)/tricalcium Phosphate Composite Scaffold and Its Various Changes During Degradation in Vitro

In vitro degradation of porous PLLA/pearl powder composite scaffolds

In vitro degradation of fibrous bilayer poly-L-lactic acid scaffolds

In vivo biocompatibility and degradation of novel Polycaprolactone-Biphasic Calcium phosphate scaffolds used as a bone substitute

Mechanical, permeability, and degradation properties of 3D designed poly(1,8 octanediol-co-citrate) scaffolds for soft tissue engineering.

Next‐Gen Poly(ε‐Caprolactone) Scaffolds: Non‐Destructive In Vivo Monitoring and Accelerated Biodegradation

DEGRADATION STUDY OF POLY(LACTIC ACID) POROUS SCAFFOLD AT DIFFERENT TEMPERATURES

"Wet-State" Mechanical Properties of Three-Dimensional Polyester Porous Scaffolds

Effect of polycaprolactone impregnation on the properties of calcium silicate scaffolds fabricated by 3D printing

Degradation Behavior of Porous Calcium Phosphates

A strategy to tailor the mechanical and degradation properties of PCL-PEG-PCL based copolymers for biomedical application

Degradation of 3D-Printed Porous Polylactic Acid Scaffolds Under Mechanical Stimulus

In vitro and in vivo degradation behavior of n-HA/PCL-Pluronic-PCL polyurethane composites