Abstract:Large or carcinogenic bone defects may require a challenging bone tissue scaffold design ensuring a proper mechanobiological setting. Porosity and biodegradation rate are the key parameters controlling the bone-remodeling process. PLA presents a great potential for geometrically flexible 3-D scaffold design. This study aims to investigate the mechanical variation throughout the biodegradation process for lattice-type PLA scaffolds using both experimental observations and simulations. Three different unit-cell geometries are used for creating the scaffolds: basic cube (BC), body-centered structure (BCS), and body-centered cube (BCC). Three different porosity ratios, 50 %, 62.5 %, and 75 %, are assigned to all three structures by altering their strut dimensions. 3-D printed scaffolds are soaked in PBS solution at 37 °C for 15, 30, 60, 90, and 120 days both unloaded and under dead load. Water absorption, weight loss, and compression stiffness are measured to characterize the first-stage degradation and investigate the possible influences of these parameters on the whole biodegradation process. The strength reduction stage of biodegradation is simulated by solving pseudo-first-order kinetics-based molecular weight change equation using FEA with equisized cubic (voxel-like) elements.For the first stage, mechanical load does not have a statistically significant effect on biodegradation. BCC with 62.5 % porosity shows a maximum water absorption rate of around 25 % by the 60th day which brings an advantage in creating an aquatic environment for cell growth. Results indicate a significant water deposition inside almost all scaffolds and water content is determined to be the main reason for the retained or increased compression stiffness. A distinguishable stiffness increase in the initial degradation process occurs for 75 % porous BC and 50 % porous BCC scaffolds. Following the quasi-stable stage of biodegradation, almost all scaffolds lost their rigidity by around 44–48 % within 120 days based on numerical results. Therefore, initial stiffness increase in the quasi-stable stage of biodegradation can be advantageous and BCC geometry with a porosity between 50% and 62 % is the optimum solution for the whole biodegradation process.

Effects of Degradation Media of Polyester Porous Scaffolds on Viability and Osteogenic Differentiation of Mesenchymal Stem Cells

Effects of Porosity and Pore Size on in Vitro Degradation of Three-Dimensional Porous Poly(d,l-Lactide-co-glycolide) Scaffolds for Tissue Engineering.

In Vitro and in Vivo Degradability and Cytocompatibility of Poly(l-Lactic Acid) Scaffold Fabricated by a Gelatin Particle Leaching Method

In vitro and in vivo degradability and cytocompatibility of poly(l-lactic acid) scaffold fabricated by a gelatin particle leaching method.

Effect of Porosity on Long-Term Degradation of Poly (Ε-Caprolactone) Scaffolds and Their Cellular Response

Preparation of Hybrid Scaffold of PLGA Sponge/Fibrin Gel/BMSCs/DNA Complexes with Enhanced Property for BMSCs Differentiation

Poly(l,l-lactide-co-glycolide)/tricalcium Phosphate Composite Scaffold and Its Various Changes During Degradation in Vitro

In vitro degradation of porous PLLA/pearl powder composite scaffolds

Degradation of 3D-Printed Porous Polylactic Acid Scaffolds Under Mechanical Stimulus

Degradation and Characterisation of Electrospun Polycaprolactone (PCL) and Poly(lactic-co-glycolic acid) (PLGA) Scaffolds for Vascular Tissue Engineering

Osteochondral repair using porous poly(lactide-co-glycolide)/nano-hydroxyapatite hybrid scaffolds with undifferentiated mesenchymal stem cells in a rat model.

In vitro and in vivo degradation of poly(L: -lactide-co-glycolide) films and scaffolds

Accelerated degradation of poly(l-lactide) bone scaffold: Crystallinity and hydrophilicity

"Wet-State" Mechanical Properties of Three-Dimensional Polyester Porous Scaffolds

Proliferation and Differentiation of Human Osteoblasts Within 3D Printed Poly-Lactic-co-Glycolic Acid Scaffolds

Mechanical deviation in 3D-Printed PLA bone scaffolds during biodegradation

In vitro degradation of fibrous bilayer poly-L-lactic acid scaffolds

Modulated Degradation Rates of Bone Mineral-Like Calcium Phosphate Glass to Support the Proliferation and Osteogenic Differentiation of Bone Marrow-Derived Stem Cells

Physical and degradation properties of PLGA scaffolds fabricated by salt fusion technique

Poly(lactide-co-glycolide) Porous Scaffolds for Tissue Engineering and Regenerative Medicine

3D printed PLGA/MgO/PDA composite scaffold by low-temperature deposition manufacturing for bone tissue engineering applications