Abstract:Multipass ECAP was applied to prepare ultra-fine-grained Ti-6Al-4V alloy. The microstructure evolution and mechanical properties of Ti-6Al-4V alloy during ECAP process were discussed in this study. Grain size of Ti-6Al-4V alloy decreased significantly with the increase in the number of ECAP passes, and numerous grains with size of 200-300 nm were observed in the four-pass ECAP sample. The twinning structure plays an important role in the plastic deformation coordination mechanism, which can be reflected by the gradually increasing twins during multipass ECAP process. Moreover, the Vickers hardness and room-temperature compression strength increased with the increase in the number of ECAP passes due to the high dislocation density, grain refinement and the large number of twins. The hardness and compression strength increased from 355 HV and 1296 MPa to 392 HV and 1432 MPa, respectively. However, the ultimate strain of the four-pass ECAP sample is even higher than that of the two-pass and three-pass samples because of its uniformly refined microstructure and high twinning density. Uniform microstructure with average grain size of 1-2 μm was obtained by four-pass ECAP and following annealing treatment at 923 K for 30 min, which indicates that static recrystallization occurs in a relatively low temperature and short time. The compression experiments results show that Ti-6Al-4V alloy prepared by four-pass ECAP and following annealing treatment exhibits high comprehensive properties in both strength and plasticity at room temperature, with corresponding values of 48.8% in ultimate strain and 1400.3 MPa in strength.

Fabrication of Bulk Ultrafine Grained Titanium Alloy Via Equal Channel Angular Pressing Based Thermomechanical Treatment

Formation of Ultra-fine Grained Titanium Alloy by Equal Channel Angular Pressing

Status of Preparing Ultra-Fine Grained Titanium Alloys by Equal Channel Angular Pressing

Microstructure Evolution of TA15 Titanium Alloy Subjected to Equal Channel Angular Pressing and Subsequent Annealing at Various Temperatures

Microstructure Evolution and Mechanical Properties of a Ti–35Nb–3Zr–2Ta Biomedical Alloy Processed by Equal Channel Angular Pressing (ECAP)

A two step SPD processing of ultrafine-grained titanium

Microstructure and properties of pure Ti processed by ECAP and cold extrusion

Microstructure Evolution and Mechanical Properties of Ti-6Al-4V Alloy Prepared by Multipass Equal Channel Angular Pressing

Study of Microstructure and Mechanical Properties of Pure Titanium Processed by New Route of Equal Channel Angular Pressing

Processing of High Purity Titanium by Equal Channel Angular Pressing at Cryogenic Temperature

Ultrafine Processing of (tib+tic)/tc18 Composites Processed by ECAP Via Bc Route

Impact of Equal Channel Angular Pressing on Mechanical Behavior and Corrosion Resistance of Hot-Rolled Ti-2Fe-0.1B Alloy

Grain refinement and properties of pure Ti processed by warm ECAP and cold rolling

Influence of ECAP Processing Parameters on Microstructure of TA15 Titanium Alloy

Evolution of microstructure, macrotexture and mechanical properties of high strength biomedical TA4 pure titanium during multi-pass ECAP

Microstructure evolution and mechanical properties of an AZ61 alloy processed with TS-ECAP and EPT

Cryogenic temperature equal channel angular pressing of pure titanium: microstructure and homogeneity

Microstructure and Properties of Ultrafine-Grained Aluminum-Based Alloy Processed by Equal Channel Angular Pressing

Microstructural Evolution and Thermal Stability of Ultra-Fine Grained Al-4mg Alloy by Equal Channel Angular Pressing

Deformation Behavior of Pure Titanium Powder Extruded by Single-Pass Equal Channel Angular Pressing at Room Temperature

Structure and mechanical properties of commercial purity titanium, processed by ECAP at room temperature