Fabrication and characterization of FePt magnetic nanofibers via electrospinning technique
Xinlei Zhang,Weiwei Pan,Juan Dong,Qingfang Liu,Jianbo Wang
DOI: https://doi.org/10.1007/s10853-015-9276-6
IF: 4.5
2015-01-01
Journal of Materials Science
Abstract:L1 0 -structured platinum–iron (FePt) nanofibers were successfully synthesized by electrospinning technique, followed by calcination and reduction processes. In the preparation procedure, ferrous chloride tetrahydrate [Fe(Cl) 2 ⋅4H 2 O] and iron nitrate nonahydrate [Fe(NO 3 ) 3 ⋅9H 2 O] were, respectively, used as iron sources contained in precursor solution for electrospinning. Subsequently, the FePt nanofibers were obtained from the calcination in air and the followed reduction in hydrogen (H 2 ) of the as-spun FePt/PVP composite nanofibers. The FePt nanofibers were characterized by X-ray diffractometer, scanning electron microscopy, transmission electron microscopy, and superconducting quantum interference device magnetometry. It was found that the different iron salt used in the spinning solutions could highly affect the FePt nanofiber morphology, crystallite size, and the magnetic properties. The FePt nanofibers, resulted from the spinning solution containing iron dichloride tetrahydrate, were of better crystallinity and well-defined fibrous morphology with an average diameter of about 110 nm. Additionally, the considerably large coercivity of 10.27 kOe was recorded from the above FePt nanofibers.