Nanoporous ordered materials: Osmotically shocked.
Patrick Theato,Goran Ungar
DOI: https://doi.org/10.1038/nmat3210
IF: 41.2
2012-01-01
Nature Materials
Abstract:Soft materials surrounded by a semipermeable membrane — such as vesicles or cells — can experience an imbalance in osmotic pressure as a result of a difference in solute concentration between the two sides of the membrane. If the pressure imbalance is large — which can occur in hypotonic solutions — stress build-up can ultimately lead to membrane rupture. Yet such an osmotic shock is not exclusive to cells. Reporting in Nature Materials, Zavala-Rivera and colleagues describe an ingenious method for triggering multiple osmotic shocks in a coordinated fashion within ordered block-copolymer (BCP) films to produce a well-defined pore geometry1. The researchers show that the perforated nanostructures behave as one-dimensional photonic crystals, and that they can be used as ultrafiltration membranes and as electrodes in light-emitting devices. Linking together two or more incompatible homopolymer chains usually results in phase separation on the nanometre scale. For instance, BCPs tend to self-assemble into well-ordered bulk morphologies — such as spheres or cylinders of one phase in a matrix of another, as well as gyroids, lamellae or honeycombs. These structures have been transformed into ordered nanoporous materials, for instance by removing the minority phase with a selective etching process2. Although only a small number of labile blocks can be removed by etching, the use of a photocleavable linker at the junction of the BCP enables the use of practically any BCP in the formation of nanoporous materials3. However, in these approaches the dimensions and geometry of the porous structures are fixed. This is because the morphology of self-assembled BCPs primarily depends on the size ratio of the polymer blocks, which cannot be easily altered by synthetic means. To achieve pores with larger sizes, the volume of the removable block needs to be expanded. This has recently been achieved in two ways: by introducing small molecules through hydrogen bonding to the block4, and by inducing swelling of the block with a selective solvent, a method that can also cause a change in morphology5. As well as the expansion of the minority component, the latter approach also involves simultaneous plasticization of the matrix phase. For example, hot-ethanol treatment of polystyrene–block–poly(2-vinyl pyridine) (PS–b–P2VP) not only swells the P2VP phase, but also plasticizes the PS matrix, thereby enabling stress dissipation during the expansion process6. Another example is the use of supercritical CO2 — which selectively swells fluorinated domains of BCPs — to induce morphological changes to the domains and, on CO2 release, to produce porous structures7. This process is similar to classical foaming techniques, and as such it is crucial to enable a controlled and fast release of the foaming agent or solvent. The method reported by Zavala-Rivera and co-authors is also based on swelling-induced expansion of the minority phase, yet unlike previous approaches it achieves controlled rupture of the matrix1. The researchers used a polystyrene–block–poly(methyl methacrylate) (PS–b–PMMA) thin film, which forms hexagonally close-packed PMMA spheres within a PS matrix. They then broke down the PMMA block into small oligomers and slightly crosslinked the PS matrix by exposing the film to ultraviolet light. Subsequently, they immersed the film in acetic acid, a highly selective solvent for the PMMA oligomers. As the solvent permeated through the semipermeable PS matrix, it swelled the domains with PMMA oligomers, causing them to deform. Eventually, a high osmotic imbalance caused explosive rupture of the matrix around the ordered yet deformed domains. This process led to an expanded bicontinuous porous multilayer (Fig. 1a) resembling a layered rock formation (Fig. 1b). Zavala-Rivera and co-workers also proposed that the osmotic-shock explosions occurred collectively in a layer-by-layer fashion, expanding the material much like the bellows of an accordion being stretched out from one side. Interestingly, osmotic-pressure differences can be large enough to break up even highly crystalline polymers. This happens for example when a film of high-density polyethylene (HDPE) containing stacks of 20-nm-thick crystalline lamellae is swollen by styrene and irradiated with gamma rays8. Radiation-induced polymerization of styrene produces PS chains grafted onto the HDPE chains, which causes further swelling by styrene in a self-enhancing process that leads to cracking and fragmentation of the lamellar stacks of semicrystalline HDPE (Fig. 2). Perhaps preventive crosslinking, as implemented by Zavala-Rivera and co-authors, would have delayed the fragmentation. Importantly, the authors' collective-osmotic-shock approach can be applied to any ordered material containing a minority component that can be selectively degraded and solvated within a deformable matrix, provided that appropriate conditions can be found that can simultaneously degrade the minority phase and rupture the matrix while ensuring its mechanical integrity. The authors also demonstrated that a replica of the bicontinuous nanoporous films in flexible titania lamellar sheets fabricated using sol–gel chemistry could be used as electrodes in a light-emitting device. Furthermore, the rejection of an organic dye after passage through the BCP films was enhanced by a factor of 2,000 compared with that achieved by commercial ultrafiltration membranes. Considering the apparent generality of the fabrication method, the nanoporous materials may also find applications in gas purification, catalysis and sensing. Yet more than anything else, the cascading collective-osmotic-shock approach makes the fabrication of orderly nanoperforated structures shockingly easy. Download references