Experimental Investigation on Corrosion of Reinforced Concrete due to Coupled Stray Currents and Chloride Ions

CHEN Meng-cheng,WANG Kai,WU Quan-shui,Qin Zhen

DOI: https://doi.org/10.3969/j.issn.1001-8360.2013.09.018

2013-01-01

Abstract:In view of the service environments of subway engineering structures, experiments on corrosion of reinforced concrete (RC) in three different corrosion environments of stray currents, chloride ions and their combination were carried out respectively and the corrosion developing laws were investigated. Stray currents were simulated by direct currents. The results show as follows: Under the sole action of stray currents, corrosion of rebars in concrete undergoes two stages, i.e., the accelerating stage and the steady developing stage, whereas under the sole action of chloride ions, corrosion of rebars in concrete is developed slowly and steadily, and the rebar corrosion rate due to stray currents is greater than that due to chloride ions; under the coupled action of stray currents and chloride ions, since stray currents speed up transportation of chloride ions into concrete, the corrosion rate of steel in RC is increased and the time from passivating of steel to cracking of concrete cover is shortened obviously; in the service environments of subway engineering structures, the steel corrosion degree of RC depends on the stray current strength, the chloride ion concentration and the corrosion duration; the greater the stray current strength, the heavier the chloride ion concentration and the longer the corrosion duration, the more serious the corrosion of steel in RC.