Abstract:Superhydrophobic cotton fabrics were successfully prepared by grafting modification of cotton fabrics through carbene polymer induced crystallization and self-assembly. The structures and properties of grafted polymer crystals on the surface of cotton fabrics were examined by scanning electron microscopy (SEM), fourier transform infrared spectroscopy (FT-IR) and nuclear magnetic resonance spectroscopy (NMR). The surface grafting positions with diazo active groups were pre-constructed on the fibers. The 3,3,4,4,5,5,6,6,6-nonfluorohexyl diazoacetate (Hex(C4F9)DA) and 3,3,4,4,5,5,6,6,7,7,8,8,8-tridecafluorooctyl diazoacetate (Oct(C6F13)DA) were synthesized as precursors followed by carbene grafting to fiber. Under different reaction conditions, the polymer crystallized on the fiber surface and produced different morphologies such as solid rods, hollow rods, and spheres. The surface morphology was controllable by changing the medium, reaction time and kinetic conditions. When 3,3,4,4,5,5,6,6,6-nonfluorohexyl diazoacetate (Hex(C4F9)DA) was used as the precursor and tetrahydrofuran (THF) as the solvent, the grafted cotton fabric exhibited excellent hydrophobic properties with a water contact angle of 152°. When 3,3,4,4,5,5,6,6,7,7,8,8,8-tridecafluorooctyl diazoacetate (Oct(C6F13)DA) was used as the grafting precursor, THF or THF/EtOH mixed solvent was used as the reaction medium, the contact angle of the as-prepared cotton fabric to water was measured to be 151° and 154°, respectively. During the carbene grafting polymerization, the solvent has a significant influence on the morphology of the grafted polymer. The WCA and EDS results suggest that the synergistic effect between the rough structure of the grafted cotton fabric surface and the low surface energy of fluorine element made the fabric super-hydrophobic.

Structure and Properties of Cotton Grafted Using Trifluoroethyl Methacrylate Via ATRP Method

Surface Modification of Cotton Fabric to Create Water Repellence Property Via Atom Transfer Radical Polymerization

Structure and Properties of Silk Grafted with Acrylate Fluoride Monomers by ATRP

Controlled grafting superhydrophobic cellulose surface with environmentally-friendly short fluoroalkyl chains by ATRP

Surface-initiated Atom Transfer Radical Polymerization on Cotton Fabric in Water Aqueous

Structure And Properties Of Silk Fibroin Grafted With Dimethylaminoethyl Methacrylate By Atrp In Water Aqueous

Cotton fabric modification for imparting high water and oil repellency using perfluoroalkyl phosphate acrylate via γ-ray-induced grafting

A "grafting through" strategy for constructing Janus cotton fabric by mist polymerization

Technological Process Optimization Experiment on Water Repellence Finishing of Silk Fabric Grafted with Fluorinated Acrylate via ATRP Method

Surface Grafting Modification of Silk Fibroin via ARGET ATRP Method

Radiation Induced Graft Polymerization of a Fluorinated Acrylate Onto Fabric

Structure and Properties of Silk Grafted with N,N-Dimethylaminoethyl Methacrylate by ATRP

Technological Conditions of Silk Grafting Modification Using Atom Transfer Radical Polymerization Method

Preparation of Super-Hydrophobic Cotton Fabrics with the Controllable Roughening Fiber Surface by Carbene Polymerization Grafting

Modification of Silk Fiber Via Emulsion Graft Copolymerization with Fluoroacrylate

Studies of Fluorinated Methylacrylate Copolymer on the Surface of Cotton Fabrics

Grafting of 2-Diethylaminoethyl Methacrylate Onto Silk by ATRP

Structures of Silk Fibers Grafted with Hexafluorobutyl Methacrylate

Antibacterial cotton fabric prepared by a “grafting to” strategy using a QAC copolymer

Preparation of Fluoroalkylsilyl Polymethacrylates and Their Waterproof Application on Cotton Fabrics

Hydrophobic Modification of Wood Via Surface-Initiated ARGET ATRP of MMA