Abstract:An investigation is given on the influence of heat treatment by the microstructural characteristics and tensile properties of a new high strength alloy Ti-2Al-9.2Mo-2Fe. Both of the alpha/beta and p solution treatment (alpha/beta-ST and beta-ST), then aged at temperatures ranging from 400 degrees C to 600 degrees C, were prepared. The primary a phases having 2-5 mu m are formed during the alpha/beta-ST and restrain the size of beta grains below 10 mu m. As a result of the fine beta grains, the alpha/beta-ST contributes a higher strength than the beta-St The coexistence of alpha" and athermal omega phase is found in the beta-ST and water quenched samples. However, these have little influence on the alloy hardening. After aging, the alloys in the alpha/beta-ST and beta-ST condition reveal the phase transformation of beta to isothermal omega, and beta to a depending on the aging temperature. Although the primary alpha phase formed during the alpha/beta-ST increases the stability in the beta matrix, and the isothermal omega phase also appears to occur during aging at 400 C and 450 degrees C for 2 h. These phenomena are less common in beta titanium alloys, when treated in the alpha/beta-ST and aged at lower temperatures. The isothermal omega phase formed in both conditions results in high strength levels (1600 MPa of ultimate strength) with much ductility loss (2.5-4.5% of elongation) as a result of the superior hardening effect and brittleness of omega phase. However, the secondary a phase with the size of 1-3 mu m leads to attractive combinations of strength and ductility (1200-1400 MPa of ultimate strength with 7.5-12.5% of elongation). The reason for that is too fine a phase below 1 mu m tends to result in ultra-high strength with much ductility loss. As a whole, the alloy can be heat treated to obtain excellent balances of strength and ductility, and provided abundant stress levels with optional ductility as a usable material. (C) 2013 Elsevier B.V. All rights reserved.

Evolution of the Secondary Α Phase Morphologies During Isothermal Heat Treatment in Ti-7333 Alloy

Phase Transformation And Microstructure Evolution In Near-Beta Ti-7333 Titanium Alloy During Aging

Study of PrimaryαPhase Transformation in a New Beta Titanium Alloy with Different Cooling Conditions

Phase Transformation and Microstructure Evolution in Near-β Ti-7333 Titanium Alloy During Aging

Hot Deformation Behavior of a Novel Near-β Titanium Alloy Ti-5.5Mo-6V-7Cr-4Al-2Sn-1Fe in (α+β) Phase Region

Precipitation of Secondary Phase and Phase Transformation Behavior of a Solution-Treated Ti-6Al-4V Alloy During High-Temperature Aging

Thermomechanical Processing of a Near-Β Titanium Alloy and Effects on Microstructure and Tensile Properties

Phase Precipitation Behavior During Isothermal Deformation in Β-Quenched Near Beta Titanium Alloy Ti-7333

Microstructural Evolution And Precipitation Mechanism Of Alpha-Phase In Ti-55531 Alloy Aged At High Temperature

Isothermal α Precipitation and Evolution in a Hot-Rolled near β Titanium Alloy

Precipitation of Α Phase and Its Morphological Evolution During Continuous Heating in a Near Β Titanium Alloy Ti-7333

Influence Of Heat Treatment On Microstructure And Tensile Property Of A New High Strength Beta Alloy Ti-2al-9.2mo-2fe

Transformation of Phase and Microstructure in Ti-1300 Alloy During Isothermal Aging

Effect of Aging Temperature on Microstructures and Precipitation Hardening in Ti1023 and Ti5553 Alloys

Effects of Aging Treatment on Microstructure Evolution and Mechanical Properties of Ti-6Al-3Nb-2Zr-Mo Alloy

Influence of Solution Treatment on Microstructure of A Near-Alpha Titanium Alloy

Microstructural Evolution During Post-Heat Treatment and Its Effect on the Mechanical Properties of Directed Energy Deposited Near Β Titanium Alloy

Evolution of Equiaxed Alpha Phase During Heat Treatment in a Near Alpha Titanium Alloy

Phase Transformation and Kinetics in Metastable Β Titanium Alloy During Isothermal Treatment

The phase transformation during the low temperature aging and low rate heating process of metastable titanium alloys

Characterization of Α Phase in A Near Β Titanium Alloy Ti‐7Mo‐3Nb‐3Cr‐3Al During Hot Deformation