Abstract:In this paper, we report a simple melt impregnation method by using cheap mesophase pitches (MPs) as carbon precursors to prepare ordered mesoporous carbon with ordered graphitized pore walls at low temperature. This facile procedure includes melting MPs at 140 degreesC and impregnation of the melt into hexagonal or bicontinuous cubic mesoporous silica templates. After the removal of silica templates by HF solution, ordered mesoporous carbon materials with replica structures of 2-D hexagonal p6mm or cubic Ia (3) over bard symmetry were derived. The pore walls of the hexagonal mesoporous carbon products are composed of graphitized domains with the (002) crystallographic plane of the graphite perpendicular to the long axis of the carbon nanorods. Theoretical computations show that negatively charged O atoms of Si-OH and Si-O-Si from the surface of mesoporous silica channels can interact with the positive charged H atoms of the MPs, which makes the stacking units incorporate into the pores with the (002) plane vertical to the channels, and finally the oriented periodicity of the graphite domains is formed. N(2) sorption measurements show that the materials possess no micropores. For the bicontinuous cubic mesoporous carbon, HRTEM images show that the material is a true replica framework of la3 ($) over bard symmetry. The graphitized structure of the pore walls seems to have an orientation related to the bicontinuous pore structure, which could not be simply defined based on current TEM results. Graphitized carbon nanofiber bundles with a uniform diameter of about 7 nm were obtained by using Fe(2)O(3) nanoparticle doped mesoporous silica as a template. A spiral graphite structure was observed for the materials. Cyclic voltammetry measurements show low charge/discharge currents for the graphitized materials compared to the amorphous mesoporous carbon, further confirming the anisotropic character of the graphitized mesoporous carbons. The method can be widely applied to the hard-templating synthesis of graphitized carbon nanostructures and other doped carbon nanomaterials.

Synthesis of Porous Graphitic Carbon from Mesocarbon Microbeads by One-Step Route

Preparation and Characterization of Mesocarbon Microbeads by the Co-Polycondensation of High-Temperature Coal Tar Pitch and Coal Pyrolytic Extracts

Sub-millisecond lithiothermal synthesis of graphitic meso–microporous carbon

Sustainable mechanochemical synthesis of catalytically graphitized mesoporous carbons

Porous Graphitic Carbons Prepared by Combining Chemical Activation with Catalytic Graphitization

Cordierite Reinforced Graphite Nanocomposite with Superior Adsorption Capacity Synthesized by In-Situ Carbon-Bed Pyrolysis Method

Solution-processable porous graphitic carbon from bottom-up synthesis and low-temperature graphitization

Catalytic Graphitization for Preparation of Porous Carbon Material Derived from Bamboo Precursor and Performance as Electrode of Electrical Double-Layer Capacitor

A Simple Melt Impregnation Method to Synthesize Ordered Mesoporous Carbon and Carbon Nanofiber Bundles with Graphitized Structure from Pitches

Nickel Acetate-Assisted Graphitization of Porous Activated Carbon at Low Temperature for Supercapacitors With High Performances

One-Step Nanocasting Synthesis of Ordered Mesoporous Carbon with Graphitic Frameworks

Controllable Morphologies and Electrochemical Properties of Graphitizing MCMB-based Hybrids with Nanostructure Via a Simple Chemical Vapor Deposition Method

Preparation of mesoporous carbon with adjustable diameter and pore size

Ordered mesoporous graphitized pyrolytic carbon materials: Synthesis, graphitization, and electrochemical properties

Fabrication and Characterization of Mesoporous Carbon Nanosheets Using Halloysite Nanotubes and Polypyrrole Via A Template-Like Method

Molecular Engineering toward High‐Crystallinity Yet High‐Surface‐Area Porous Carbon Nanosheets for Enhanced Electrocatalytic Oxygen Reduction

A novel mesoporous carbon with straight tunnel-like pore structure for high rate electrochemical capacitors

Template Synthesis of Mesoporous Carbon Microfibers As A Catalyst Support for Methanol Electrooxidation

Micro-mesoporous Graphitic Carbon Nanofiber Membranes

Sustainable catalytic graphitization of biomass to graphitic porous carbon by constructing permeation network with organic ligands

Preparation of mesocarbon microbeads from coal tar pitch with blending of biomass tar pitch