Effects of heat treatment on structure and magnetic properties of nanocrystalline Mn-Zn ferrite

胡平,王快社,王华,何欢承,杨帆,康轩齐,王鹏洲
DOI: https://doi.org/10.13251/j.issn.0254-6051.2013.08.004
2013-01-01
Abstract:Nanocrystalline Mn-Zn ferrite powder was prepared by nitrate-citrate auto-combustion synthetic method and subsequently annealed at different temperatures in muffle furnace without protective atmosphere. The effects of heat treatment temperature on crystalline phase formation, microstructure and magnetic properties of the Mn-Zn ferrite were investigated by FTIR, TG-DTA, XRD, SEM and VSM. The results show that when annealed above 550°C in air, the ferrite decomposes to Fe2O3 and Mn2O3, and has poor magnetic properties, when annealed above 1100°C, Fe2O3 and Mn2O3 are dissolved, and the sample annealed at 1200°C is composed of pure ferrite phase with good crystallinity and uniform grain and has larger saturation magnetization (Ms=48.15 emu·g-1) compared with that of the auto-combusted ferrite powder.