Experimental investigation into transverse crashworthiness of CFRP adhesively bonded joints in vehicle structure

Wenyan Wu,Qiang Liu,Zhijian Zong,Guangyong Sun,Qing Li
DOI: https://doi.org/10.1016/j.compstruct.2013.07.009
IF: 6.3
2013-01-01
Composite Structures
Abstract:This paper aims to investigate the crashworthiness of adhesively bonded joints for composite panels under transverse (off-plane) loading. The adherends were made of plain weave carbon fiber reinforced plastics (CFRP) composites; and epoxy adhesive Hysol 9432 was used for bonding. The three point bending tests were conducted first to examine the influence of overlap geometrical parameters, and the impact tests were then carried out to explore the damage process under different impact energies. The results show that the ultimate load and stiffness increase with the increasing overlap width and length in the three point bending tests, and the influence caused by overlap width is more significant. The energy absorption and crack length increase as the impact energy increases in the low velocity impact tests. It is found that for the joint with 20mm overlap width and 30mm overlap length, the ultimate load and absorbed energy are 725N and 4.03J respectively under the dynamic transverse impact respectively, which are 1.57 times and 1.07 times higher than those under the static transverse bending. By observing micrographs of the failure surface of the specimens tested, the failure mode of CFRP adhesively bonded joints was mixing cohesive and adhesive fracture.
What problem does this paper attempt to address?