Ash fusion temperature and crystal composition of multi-component coal ash
MIAO Miao,KONG Hao,ZHANG Man,WU Yuxin,YANG Hairui,ZHANG Jiansheng
DOI: https://doi.org/10.11949/0438-1157.20190140
2019-01-01
Abstract:The ash fusion temperature of coal at high temperature is an important parameter for the efficient and safe operation of coal gasifiers. The equipment of ash fusion temperature was used to measure the ash fusion temperatures of the oxide components composed of SiO2, Al2O3, Fe2O3, MgO, and CaO with different proportions. Five variables composed of Si/Al, Si+Al, Fe2O3, MgO, and CaO were selected to verify the effect of the change on the coal ash fusing characteristics and the range of variables cover most domestic coal ash. Factsage was used to calculate the liquidus temperature of coal ash components, and to obtain the solid phase ratios of each crystal in each slag system and the simulation results are verified by experiments. With the contents of CaO, Fe2O3 and Si/Al increase, the ash fusion temperature gradually decreases while with the content increasing of Si+Al and MgO, the ash fusion temperature of the coal ash gradually increases. The ash fusion temperature varied with the contents of the oxide components and was closely related to the corresponding liquidus temperature, which was always higher than the ash fusion temperature about 200℃. Factsage was also used to predict the crystal compositions of the slag system at different temperatures. It could be concluded that there was no necessary relationship between the transformation of different slag systems with the change of a certain variable, and further analysis was needed for the slag system dominated by a specific factor. In the crystal phase experiment, after the slag was fused, quenching could be performed quickly to maintain the original crystal form at the high temperature. When X-ray diffraction analysis was completed, the precipitation ratios of different crystals at various temperatures could be obtained, which was in good agreement with the simulation results. The differences between the simulation and experimental results were also explored. The effects of different oxide compositions on the slag solidification ratios were investigated. The conclusion of this paper lays a foundation for further analysis of the product and characteristics of the molten state of multi-oxide system, and is of great significance for the optimization design operation of gasifier.