Synthesis and Magnetic Properties of Non-Stoichiometric ${\rm Co}_{2}{\rm Z}$ Hexaferrite

Lijun Jia,Huaiwu Zhang,Lei Xu,Fiming Bai,Baoyuan Liu

DOI: https://doi.org/10.1109/tmag.2013.2245314

IF: 1.848

2013-01-01

IEEE Transactions on Magnetics

Abstract:A several of non-stoichiometric Co(2)Z hexaferrites with composition of Ba3(1+x)Co2Fe24O39+x (x = -0.20 - 0.20) have been synthesized. Their structural and magnetic properties have been characterized. It is found that the increase of Ba2+ amount is beneficial to the formation of Z-type phase and the reduction of sintering temperature. Excess Ba2+ ions distributed in the large interspace along a-axis orientation enhance the grain growth and densification due to the activation of lattice, which in turn first lead to an increase and then a decrease of saturation magnetization. Meanwhile, owing to the compact and uniform microstructures, and high sintering density, relatively high initial permeability was obtained in the samples with proper Ba2+ amount while magnetic loss no significant change. On the contrary, when x < 0, the Z-type crystal structure of (B2S4B1S4)(2) becomes unstable because of Ba2+ deficiency. The impurity phase was detected in these samples. Saturation magnetization decreases and coercive force increase with Ba2+ deficiency. Consequently, the initial permeability decreases.