Abstract:This study deals with the Nb–niobium silicide-based composites developed by the hot-pressing of Nb–Si–Ti ternary powder mixtures with a fixed Ti addition (6at.%) and Si content ranging from hypereutectic (11at.%) to near-eutectic compositions (18at.%). The effects of Si content, Ti addition and strain rates on the sample microstructural characterization, flexural strength, fracture toughness, quasi-static compressive deformation and failure processes were investigated. It was revealed that the volume fraction of silicides increased with increasing Si content, and most of the Ti atoms dissolved into the niobium silicides to form (Nb,Ti)5Si3 solid solutions instead of binary titanium silicides. The experimental evidence showed that a moderate improvement in the flexural strength, fracture toughness and compressive yield stress of the composites was achieved by the addition of Ti. Higher Si additions produced a much more remarkable enhancement in the compressive yield stress and bulk hardness, whereas both the flexural strength and fracture toughness decreased with increasing Si content owing to the existence of residual porosities in the samples. The composites showed remarkable superiority to the arc-melted Nb–Si alloys and monolithic niobium silicides in fracture toughness (8.3–13.0MPam vs. 4.5MPam), where the toughening effect was attributed mainly to crack bridging and crack deflection by the remaining ductile Nb phase. Moreover, quasi-static uniaxial compression tests at strain rates between 10–5 and 10–3s−1 indicated that the deformation behavior and failure processes were significantly affected by Si content and strain rates. The strain-rate-hardening behavior for all the strain rates was observed in the composite materials and the strain-rate sensitivity decreased with increasing Si content. At a lower strain rate, the composite materials with a hypoeutectic Si composition failed with a pseudoplastic response and at an angle of ∼45° off the compressive loading direction. However, in the case of higher strain rate and Si content, the brittle failure in the samples occurred through vertical splitting and spalling of fragments.

Effect of silicon on ultra-low temperature toughness of Nb-Ti microalloyed cryogenic pressure vessel steels

Influence of Silicon Addition on the Low Temperature Toughness of Pressure Vessel Steels

Effect of Silicon Content on Carbide Precipitation and Low-Temperature Toughness of Pressure Vessel Steels

Effect of Ti miroalloying on the low temperature toughness of 3.5Ni steel

Effects of Carbon and Niobium on Microstructure and Properties for Ti Bearing Steels

Effect of Tempering Temperature on the Low Temperature Toughness of the Cr‐Mo Alloyed Pressure Vessel Steels

Microstructure and mechanical properties of a low carbon carbide-free bainitic steel co-alloyed with Al and Si

Microstructural and mechanical characterization of Nb-based in situ composites from Nb–Si–Ti ternary system

Formation Mechanism and Effect on the Mechanical Properties of TiSi Phase for Ti-5Al-5Mo-5Cr-3Nb-2Zr Alloyed by Silicon

Effects of Silicon Content and Tempering Temperature on the Microstructural Evolution and Mechanical Properties of HT-9 Steels

Effects of the microstructure and minor elements on the fracture toughness of Nb-Si alloy

Effects of niobium and heat treatment on microstructure and mechanical properties of low carbon cast steels

Effect of Nb on Microstructural Evolution and Mechanical Properties of Hot‐Rolled Quenching and Partitioning Steels Containing Bainite

Effect of Heat Treatment on Microstructure and Mechanical Properties of Nb-containing Cryogenic Steels

Synergistic Effect of Zr and Ti on Microstructure and Properties for Nb Si Based In-Situ Composites

Formation Mechanism of Tisi Phase and Silicide Kinds on Microstructure and Mechanical Properties for Ti-5al-5mo-5cr-3nb-2zr Alloyed by Silicon

Microstructures and Mechanical Properties of Bearing Steels Modified for Preparing Nanostructured Bainite

Effects of Alloying on the Microstructures and Mechanical Property of Nb-Mo-Si Based in Situ Composites

Influence of silicon addition on intercritical annealing process and tensile properties of medium Mn steel

Effect of Nb Precipitates and Reversed Austenite Formed by QLT Process on Microstructure and Mechanical Properties of Nb-Bearing 7Ni Cryogenic Steel

Enhanced fracture toughness of silicon nitride ceramics at cryogenic temperatures