Abstract:In order to prevent the formation of large size intermetallic compounds during the TiAl-based alloy brazing, a specially designed heating process, which was established based on the analysis of Ti-Al-Ag ternary phase diagram, was presented and validated. The associated mechanism and process were proposed as follows: (i) a special dwell period was installed at the early stage during the melting of the filler metal for the generation of a weak primary AlCu2Ti intermetallic layer; (ii) with initial heating up, Ag atoms in the filler would diffuse into the TiAl substrate through the weak AlCu2Ti layer and a new liquid phase of Ti-Al-Ag would form due to the combined effects of thermal disturbance, convection and concentration gradient; (iii) the primary intermetallic compounds would be broken into irregular particles and pieces which were pushed into the molten filler; (iv) with heating up to the peak temperature, the intermetallic particles would disperse uniformly in the brazing seam, resulting in a brazing seam with a dispersive distribution of the intermetallic compound particles. To verify the feasibility of the proposed method, the vacuum brazing of a TiAl-based alloy and a 42CrMo steel was conducted within a temperature range of 1033∼1173 K and a brazing time range of 100∼300 s. Microstructures of the brazed joints were examined by optical microscopy, scanning electron microscopy (SEM) as well as energy dispersive spectrum (EDS). The results show that an intermetallics particles reinforced TiAl/steel brazing seam can be obtained by the proposed heating process.

Dissolution of TiAl Alloy During High Temperature Brazing

Development of interface reaction layer between TiAl alloy and 42CrMo brazing joints and its effect on mechanical property

Brazing of Ti2AlNb based alloy with amorphous Ti-Cu-Zr-Ni filler

Effect of Brazing Temperature on Microstructure and Mechanical Properties of TiAl/ZrB2 Joint Brazed with CuTiZrNi Filler

Microstructural Evolution and Mechanical Properties of Vacuum Brazed Ti 2 AlNb Alloy and Ti60 Alloy with Cu75 P T Filler Metal

Vacuum Brazing Effect on the Interlayer Failure Behavior of TiAl/GH3536 Hetero-Thin-walled Structure with BNi-2 Interlayer

Brazing Ti-48Al-2Nb-2Cr Alloys with Cu-Based Amorphous Alloy Filler

Brazing of Al2O3 to Ti–6Al–4V Alloy with in Situ Synthesized TiB-whisker-reinforced Active Brazing Alloy

Evaluation of Microstructure and Mechanical Properties of TiAl/HI-TEMP 820/ SCM440H Materials Manufactured through Vacuum Brazing according to Process Temperature

Brazing ZrB2-SiC Ceramics to Ti6Al4V Alloy with TiCu-based Amorphous Filler

Microstructure and properties of the TiAl/GH3030 dissimilar joints vacuum-brazed with a Ti-based amorphous filler metal

Vacuum brazing TiAl intermetallics to GH3030 alloy with a multi-component Ti-based filler metal

Characteristics of reaction phases and effects of phases on mechanical properties of TiAl/42CrMo steel brazed joint

Interfacial structure and properties of reactive brazing joints of TiAl/Ni-based alloy

Brazing TiAl intermetallics using TiNi–V eutectic brazing alloy

Understanding the oxidation behavior of TiAl alloy joints brazed using Ti and Ni based filler

Mechanism and Process of the Intermetallic Compound Particles Reinforced Tial/Steel Brazing Seam

Vacuum Brazing of Ti6Al4V Alloy to 316L Stainless Steel Using a Ti-Cu-based Amorphous Filler Metal

Interfacial features of TiAl alloy/316L stainless steel joint brazed with Zr−Cu−Ni−Al amorphous filler metal

Microstructural Evolution and Mechanical Properties of Ti2AlNb/GH99 Superalloy Brazed Joints Using TiZrCuNi Amorphous Filler Alloy

Microstructure evolution and mechanical properties of TiAl/GH536 joints vacuum brazed with Ti–Zr–Cu–Ni filler metal