Vacuum Brazing Effect on the Interlayer Failure Behavior of TiAl/GH3536 Hetero-Thin-walled Structure with BNi-2 Interlayer

Y. Luo,Z. H. Li,Y. Z. Liu,X. G. Song,S. P. Hu,W. Fu,J. Cao

DOI: https://doi.org/10.1016/j.tws.2022.110492

IF: 5.881

2023-01-01

Thin-Walled Structures

Abstract:In this work, BNi-2 interlayer was used to fabricate a thin-walled structure consisted of TiAl-based alloy and GH3536 alloy by vacuum brazing method and the erosion formation mechanism of TiAl/BNi-2/GH3536 thin-walled structure was discussed. The effects of brazing temperature, holding time and the thickness of interlayer on the dissolution height of GH3536 base metal, the size of brazing fillet, typical microstructural evolution and the mechanical properties of the brazed thin-walled structure were investigated in detail. When the optimized brazing parameter (1040 degrees C for 5 min) was selected and the interlayer thickness increased to 200 mu m, the maximum height of brazing fillet, dissolution height of GH3536 base metal and tensile strength of thin-walled structure achieved 420 mu m, 1000 mu m and 620 MPa, respectively. Due to the reaction between molten BNi-2 interlayer and TiAl-based alloy, the erosion readily forms for TiAl/GH3536 thin-walled structure than GH3536 thin-walled structure, especially at a relatively high brazing temperature.