Abstract:A high-temperature, high-cycle fatigue test was conducted on a nickel-based single-crystal superalloy with a pore structure. Optical and scanning electron microscopy were utilized to examine the crack propagation paths and fatigue fracture surfaces at the macro and micro scales. The analysis of crack initiation and propagation related to the pore structure facilitated the development of a crack shape factor reflecting these distinct fracture behaviors. Predictions about the high-cycle fatigue stress experienced by the specimen were made, accompanied by an error analysis, providing critical insights for precise stress calculations and structural optimization in engine blade design. The results reveal that high-cycle fatigue cracks originate from corner cracks at pore edges, with the initial propagation displaying smooth crystallographic plane features. Subsequent stages show clear fatigue arc patterns in the propagation zones. The fracture surface exhibits the significant layering of oxide layers, primarily composed of NiO, with traces of CoO displaying columnar growth. AL2O3 is predominantly found at the interfaces between the matrix and oxide layers. Short and straight dislocations near the oxide layers and within the matrix suggest that dislocation multiplication and planar slip dominate the slip mechanisms in this alloy. The orientation of the fracture surface is mainly perpendicular to the load direction, with minor inclined facets in localized areas. Correlations were established between the plastic zone dimensions at the crack tips and the corresponding fatigue stresses. Without grain boundaries in single-crystal alloys, these dimensions are easily derived as parameters for fatigue stress analysis. The selected crack shape factor, "elliptical corner crack at pore edges", captures the initiation and propagation traits relevant to porous structures. Subsequent calculations, accounting for the impact of oxide layers on stress assessments, indicated an error ratio ranging from 1.00 to 1.21 compared to nominal stress values.

Quantitative Analysis on Fatigue Fracture of Spray Formed Gh738 Alloy

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Investigation of fatigue mesoscopic mechanical properties of a nickel-based superalloy by instrumented microindentation measurements

Fatigue Crack Growth Behavior of Spray Formed GH738 Alloy

Fatigue Life Prediction of Nickel-Based GH4169 Alloy on the Basis of a Multi-Scale Crack Propagation Approach

Fractograph examination of superalloy GH4169 at low cycle fatigue

Statistical Analysis Methods of Fatigue Crack Growth Rate

Fatigue and Fracture Behaviors of Nickel-Based Forging Gh4169 Superalloy and Optimization of Model Parameters

High Temperature Low-Cycle Fatigue, Deformation Microstructure and Final Fracture Behavior of a Nickel-Base Superalloy

An analysis of fatigue crack features at various crack lengths through mating fracture surface pairs

Probability Analysis of Widespread Fatigue Damage in LY12-CZ Aluminum Alloy Single-Row Seven-Hole Plate

Fatigue Crack Propagation Life Prediction of GH4169 Under Biaxial Load Based on Cruciform Specimen

High cycle fatigue behavior and numerical evaluation of Alloy 690TT steam generator tube

Low-Cycle Fatigue Behavior and Fracture Mechanism of HS80H Steel at Different Strain Amplitudes and Mean Strains

An Experimental Methodology for Quantitative Characterization of Multi-Site Fatigue Crack Nucleation in High-Strength Al Alloys

Estimation of Low-Cycle Fatigue Lifetime in Aluminum-Silicon-Magnesium Alloy of Cylinder Heads based on Striation Marks as Failure Features of Fracture Surfaces and Paris Crack Growth Law

Investigation of Fatigue Small Crack Propagation Behavior in Superalloy FGH96 under Different Stress Ratios

High-temperature Fatigue Crack Propagation Study of Superalloy GH4169 by Single-Lens 3D Digital Image Correlation

High-Cycle Fatigue Fracture Behavior and Stress Prediction of Ni-Based Single-Crystal Superalloy with Film Cooling Hole Drilled Using Femtosecond Laser

Competitive Fracture Mechanism and Microstructure‐Related Life Assessment of GH4169 Superalloy in High and Very High Cycle Fatigue Regimes

Fatigue crack nucleation behavior in nickel-based PM alloy