Effect of carbon fiber on the braking performance of copper-based brake pad under continuous high-energy braking conditions
Peng Zhang,Lin Zhang,Peifang Wu,Jingwu Cao,Cairang Shijia,Dongbin Wei,Xuanhui Qu
DOI: https://doi.org/10.1016/j.wear.2020.203408
IF: 4.695
2020-10-01
Wear
Abstract:<p>The braking performance of copper-based brake pads containing different carbon fiber (CF) content was evaluated on a reduced scale dynamometer. The results show that the introduction of CF has a pronounced impact on the microhardness and plastic deformation resistance of the tribo-film. Compared with graphite, nano CFs has higher specific surface energy and is easy to react with iron to form cementite. On the one hand, the cementite containing iron particles in the sub-friction surface has high strength, which plays a strong supporting role on the friction surface; on the other hand, the cementite participating in the formation of the tribo-film also strengthens the tribo-film and reduces the oxidation degree of iron. All of those contribute to the formation of tribo-film with high plastic deformation resistance, which imparts the low transfer rate of tribo-film in the process of high-energy braking, so as to stabilize the friction coefficient and reduce the wear loss. In the range of 0–1.2 wt% CF, the 0.4 wt% CF can make the copper-based brake pad exhibit the best wear resistance and the most stable friction coefficient (0.357–0.372) during continuous high-speed emergency braking.</p>
engineering, mechanical,materials science, multidisciplinary