Abstract:Abstract Mesoporous silica (MS) was prepared through a simple self‐assembly procedure under alkaline condition with tetraethyl orthosilicate (TEOS) as SiO 2 precursor and cetyltrimethyl ammonium bromide (CTAB) as the template. A series of shape‐stabilized composite phase change materials (ss‐CPCMs), using polyethylene glycol 6000 (PEG6000) as the PCM and MS as the matrix with different mass percentage of PEG6000 loadings, was prepared through a vacuum impregnation method. N 2 adsorption‐desorption analyzer measurement showed the specific surface area and average pore size of the as‐prepared porous silica were determined to be 760 m 2 /g and about 3 nm, respectively. Differential scanning calorimetry (DSC) measurements indicated that the melting peak temperatures and latent heats of melting of the composites are varied from 52.3°C to 62.6°C and 32.9 to 186.4 J/g (PEG6000 mass fractions: 0%‐80%), which was proportional to PEG6000 content. Fourier‐transform infrared (FT‐IR) spectroscopy results implied that only the physical interaction existed between the PEG6000 and SiO 2 matrix. The shape‐stability measurements suggested the composite with the 70% mass loading of PEG6000 can still maintained the original shape and no leakage were observed above the much higher melting temperature of PEG6000 (105°C). Thermal cycling test showed that the ss‐CPCM had good thermal reliability and chemical stability although it was experienced 500 melting and cooling cycles. Moreover, the thermal decomposition temperature of the composites (393.2°C) was much larger than the melting temperature of pure PEG6000 (62.6°C), which indicated that composite presented excellent thermal stabilities and was suitable for thermal energy storage applications.

Influence of SiO 2 pore structure on phase change enthalpy of shape-stabilized polyethylene glycol/silica composites

Confinement effect of SiO 2 framework on phase change of PEG in shape-stabilized PEG/SiO 2 composites

Polyethylene glycol/silica (PEG@SiO2) composite inspired by the synthesis of mesoporous materials as shape-stabilized phase change material for energy storage

Effect Of Polyethersulfone On The Mechanical And Rheological Properties Of Polyetherimide-Modified Epoxy Systems

Shape-stabilized Phase Change Materials Based on Polyethylene Glycol/porous Carbon Composite: the Influence of the Pore Structure of the Carbon Materials

The Shape-Stabilized Phase Change Materials Composed Of Polyethylene Glycol And Various Mesoporous Matrices (Ac, Sba-15 And Mcm-41)

The dependence of phase change enthalpy on the pore structure and interfacial groups in hydrated salts/silica composites via sol-gel.

The preparation of a green shape-stabilized composite phase change material of polyethylene glycol/SiO 2 with enhanced thermal performance based on oil shale ash via temperature-assisted sol–gel method

Preparation and thermal properties of shape‐stabilized polyethylene glycol/mesoporous silica composite phase change materials for thermal energy storage

EFFECT OF POLYETHYLENE GLYCOL ON STRUCTURE AND PROPERTIES OF POROUS SILICA BLOCKS

The Influence of Interactions between Polyethylene Glycol and Graphene Oxide in Shape-Stabilized PCMs on their Phase Change Behaviors

Preparation and Characterization of Sodium Sulfate/Silica Composite As a Shape-stabilized Phase Change Material by Sol-gel Method

Polyethylene Glycol/mesoporous Calcium Silicate Shape-Stabilized Composite Phase Change Material: Preparation, Characterization, and Adjustable Thermal Property

Preparation of porous titanium dioxide foam impregnated with polyethylene glycol as shape-stable composite phase change materials

Preparation and Characterization of the Properties of Polyethylene Glycol @ Si 3 N 4 Nanowires As Phase-Change Materials

Preparation and Thermal Properties of Novel Shape-Stabilized Phase Change Materials Based on Polyethylene Glycol/Meso-Structured Onion-Like Silica Composite

Preparation and Characterization of Polyethylene Glycol/Active Carbon Composites As Shape-Stabilized Phase Change Materials

Structure and thermal properties of stearic acid/silica composites as form-stable phase change materials

Phase Change Materials Based on Polyethylene Glycol Supported by Graphene-Based Mesoporous Silica Sheets

Single-Walled Carbon Nanotube for Shape Stabilization and Enhanced Phase Change Heat Transfer of Polyethylene Glycol Phase Change Material

Polyethylene Glycol Confined in SiO2-Modified Expanded Graphite as Novel Form-Stable Phase Change Materials for Thermal Energy Storage