Abstract:Ultra-high toughness cementitious composites (UHTCC) is a kind of cementitious material reinforced by random distributed short fibers, which was proposed by Li and Leung and was designed with micromechanical principles to achieve the strain hardening behavior. This material has potential use in particular environments and structures that experience repeated or fatigue loads. Considering that the fatigue behavior of ultra-high toughness cementitious composites under compression is crucial for its application in certain conditions (e.g. airport runway and road pavements) and fatigue damage of structural components might be affected by both the flexural and compressive fatigue behaviors, the available work is rather limited and a better understanding of the compressive fatigue behavior is required. In this study, a series of monotonic and fatigue tests were performed to investigate the fatigue behavior of this material under compression. Compressive fatigue tests were conducted on 32 cylinder specimens (70 mm in diameter and 140 mm in height). The loading frequency of fatigue tests was set as 4 Hz and the maximum stress was 90%, 85%, 80%, 75%, 70% and 65% of the compressive strength with the stress ratio (the ratio between the minimum fatigue loads to the maximum fatigue load) set constant as 0.1. The S N relationship of ultra-high toughness cementitious composites was given, which indicates that the fatigue life of this material is higher than that of plain concrete and steel fiber reinforced concrete under the same stress level. It is observed that, the specimen failure mode of ultra-high toughness cementitious composites is similar to that of strain softening fiber reinforced concrete. The failure surface and damage process of this material were investigated. A new failure mode of PVA fiber with crush end was discovered with the help of SEM analysis and EDS analysis. This failure mode forms by the ruptured end of fibers experiencing repeated crushing and friction. Besides, based on the various failure modes of PVA fibers, the fatigue failure surface could be divided into three regions, including fatigue source region, transition region and crack extension region. During fatigue failure process, micro cracks initiate in the fatigue source region, propagate in the transition region and form main crack in the crack extension region.

Deformation Calculation Of Ultra-High Toughness Cementitious Composite-Concrete Beam Under Flexure Fatigue With Ultra-High Toughness Cementitious Composite Fatigue Damage Model

Study on Flexural Fatigue Life of Ultra-High Toughness Cementitious Composites under Constant Amplitude Cyclic Loading

Flexural Fatigue Damage Model Of Ultra-High Toughness Cementitious Composites On Base Of Continuum Damage Mechanics

Flexural Behaviour of UHTCC‐layered Concrete Composite Beam Subjected to Static and Fatigue Loads

Experimental study on flexural fatigue property of existing concrete beams restricted by post-poured UHTCC layer

Fatigue Prediction Model of Ultra-High-performance Concrete Beams Prestressed with CFRP Tendons

Fatigue Deformation Behavior and Fiber Failure Mechanism of Ultra-High Toughness Cementitious Composites in Compression

Numerical Method for Creep Analysis of Strengthened Fatigue-Damaged Concrete Beams

Experimental Study On Flexural Fatigue Property Of Ultra-High Toughness Cementitious Composites

Improvement of the flexural and cracking behavior of RC beams using ultra-high toughness cementitious composites(I):theoretical analysis

Investigation on Compressive Fatigue Damage Process of Ultra-High Toughness Cementitious Composites

Experimental research on fatigue behavior of prestressed ultra-high performance concrete beams with high-strength steel bars

Fatigue Damage Propagation Models for Ductile Fracture of Ultrahigh Toughness Cementitious Composites

Theoretical analysis of flexural performance of plain concrete composite beams strengthened with ultrahigh toughness cementitious composite

Calculation of Flexural Capacity for Crack-Control UHTCC/RC Composite Beams

Pseudo Strain Hardening Model of Ultra High Performance Cementitious Composites under Flexural Loading

Flexural Crack Control Performance of Existing Concrete Composite Beam Reinforced by Post-poured UHTCC

Study Progress of Fatigue Behavior of High Performance Cement-based Composite Beam

Equivalent Fatigue Constitutive Model Based on Fatigue Damage Evolution of Concrete

Continuum-based Approach for Modelling the Flexural Behaviour of Plain Concrete Beam under High-Cycle Fatigue Loads

Experimental study on the flexural performance of concrete beam strengthened with ultra high toughness cementitious composites