Axial Compressive Α-Fe2o3 Microdisks Prepared from CSS Template for Potential Anode Materials of Lithium Ion Batteries

Guo Gao,Qiang Zhang,Kan Wang,Hua Song,Peiyu Qiu,Daxiang Cui

DOI: https://doi.org/10.1016/j.nanoen.2013.03.023

IF: 17.6

2013-01-01

Nano Energy

Abstract:In this paper, α-Fe2O3 microdisks (~1.1μm in diameter, ~150nm in thickness) have been synthesized by a facile hydrothermal method using a novel NaNO3–Na2SO4 crystal salts solution (CSS) containing CNTs fragments as template. Interestingly, the synthesized α-Fe2O3 microdisks exhibit a unique axial compressive property. The small-sized CNTs fragments in α-Fe2O3 microdisks could act as a robust framework for such assemblies and endow them the axial compressive property. Owing to the existence of CNTs fragments, the α-Fe2O3 microdisks are not easily destroyed. AFM results indicate that the α-Fe2O3 microdisks could be compressed to 10–50 times than the original thickness. Electrochemical studies show that the synthesized α-Fe2O3 microdisks exhibited good cyclic stability and rate performance. The α-Fe2O3 microdisks electrode delivers a reversible specific capacity of 632mAhg31 even at a high rate of 800mAg31. When returning to the initial rate of 100mAg31, the α-Fe2O3 microdisks electrode returns to a higher capacity (968mAhg31). The unique axial compressive property of α-Fe2O3 microdisks endows that they could alleviate the pulverization and structural destruction of electrodes during the lithium ion insertion and extraction process.