Abstract:For advanced performance lithium-ion batteries (LIBs) various novel electrode materials with high energy density have been extensively investigated. Cobaltosic oxide (Co3O4), commonly used as an anode in LIBs, has attracted much interest because of its high theoretical specific capacity (890 mAh center dot g(-1)), high tap density, and stable chemical properties. However, its practical use has been hindered because of its low electronic conductivity and poor rate capability. To address these problems, we investigated a liquid phase precipitation method followed by thermal treatment and obtained a unique lamellar Co3O4 powder. Its X-ray diffraction (XRD) diffraction peaks match the standard pattern for cubic phaseCo(3)O(4) with good crystallinity. We found that the Co3O4 powder consists of many irregular sheets (1.5-3.0 mu m in diameter, 100-300 nm in thickness) with numerous poles by scanning electronmicroscopy (SEM). Additionally, the surface area was about 30.5m(2) center dot g-1, and this was calculated from BET nitrogen adsorption isotherm measurement data. Remarkably, perfect performance was obtained as evaluated by electrochemical measurements, including a high initial discharge capacity (1444.5 mAh center dot g(-1) at 0.1C) and excellent capacity retention (charge capacity after 50 cycles was still greater than 1100.0 mAh center dot g(-1) at 0.1C). However, its rate capability was still not adequate (75.3% of the first charge capacity after 50 cycles at 1C). To improve the rate capability, commercial carbon nanotubes (CNTs) mixed with the Co3O4 powder was used to enhance the electronic conductivity. The charge capacity retention ratios were 96.3% after 70 cycles at 1C and 97.0% after 50 cycles at 2C. Therefore, enhanced electrochemical performance with impressive rate capability was obtained, as expected.

Rapid-Rate Capability of Micro-/Nano-Structured Coo Anodes with Different Morphologies for Lithium-Ion Batteries

Micro-/Nanostructured Co3O4 Anode with Enhanced Rate Capability for Lithium-Ion Batteries

Nanostructured hybrid cobalt oxide/copper electrodes of lithium-ion batteries with reversible high-rate capabilities

Well-Dispersed Co/CoO/C Nanospheres with Tunable Morphology as High-Performance Anodes for Lithium Ion Batteries

Micro/nano-structure Co3O4 as high capacity anode materials for lithium-ion batteries and the effect of the void volume on electrochemical performance

Micro-spherical CoCO3 Anode for Lithium-Ion Batteries

Porous Polyhedral and Fusiform Co3O4 Anode Materials for High-Performance Lithium-Ion Batteries

Ultrasmall Co3O4 nanoparticles as a long-lived high-rate lithium-ion battery anode.

Synthesis and Modification of a Lamellar Co3O4 Anode for Lithium-Ion Batteries

Solution combustion synthesis of a nanometer-scale Co 3 O 4 anode material for Li-ion batteries

Hierarchical Co2VO4 Yolk-Shell Microspheres Confined by N-doped Carbon Layer As Anode for High-Rate Lithium-Ion Batteries

Co2+Xti1-Xo4 Nano-Octahedra As High Performance Anodes for Lithium-Ion Batteries

Electrochemical performances of nano-Co 3O 4 with different morphologies as anode materials for Li-ion batteries

Co3O4 nanosheets anchored on C/Cu porous microspheres as high-performance anode materials for lithium-ion battery

Morphology-controlled synthesis of Co3O4 porous nanostructures for the application as lithium-ion battery electrode

One-pot Synthesis of CoO/C Hybrid Microspheres As Anode Materials for Lithium-Ion Batteries

Hierarchically Structured Carbon-Coated SnO2-Fe3O4 Microparticles with Enhanced Lithium Storage Performance

Li1.1V0.9O2/C Microspheres with Isomeric Core-Shell Structure and Their Improved Lithium Storage Performance for Lithium-Ion Batteries

Micron-Sized Cobalt Niobium Oxide with Multiscale Porous Sponge-Like Structure Boosting High-Rate and Long-Life Lithium Storage

Synthesis and Study of Sn-Co-C Microsphere Composite Anode Materials for Li-ion Battery

Facile and controllable synthesis of solid Co3V2O8 micro-pencils as a highly efficient anode for Li-ion batteries