Abstract:Aim: To analyse the discolouration, radiopacity, pH and calcium ion release of Biodentine (BD), Bio-C repair (BCR) and Bio-C temp (BCT), as well as their biological effects on human dental pulp cells (hDPCs). Methodology: Sixty-four extracted bovine incisors were prepared to simulate crown fractures with pulp exposure and open root apex. The roots were filled using a mixture of agar and blood (control), and BD, BCR or BCT were placed over this mixture. Colour assessment analyses of the samples were performed before and immediately after material insertion and repeated at 30 and 90 days, using a spectrophotometer. The colour change of each specimen was evaluated at the crown and calculated based on the CIELab colour space. Digital radiographs were acquired for radiopacity analysis. hDPCs were placed in contact with different dilutions of culture media previously exposed to such materials and tested for cell viability using the MTT assay. The pH and calcium ion release of all materials were measured after 24 h; the data were assessed using one-way analysis of variance (ANOVA). Cell viability was analysed by two-way ANOVA. Differences in colour parameters and wound-healing data were assessed by two-way repeated measures ANOVA (α = 0.05). Tukey's and Dunnett's tests were used to compare the experimental groups with the control group. Results: BCR had grater radiopacity and smaller colour alteration (ΔEab/ΔE00) than the other materials tested (p < .005; p < .001). No significant differences in pH were found amongst the tested materials (p > .05). BCT was associated with the largest release of calcium ions (p < .0001). BD had cell viability similar to that of the control at the lowest dilutions, and BCR was similar to that of the control, regardless of the dilution tested (p > .05). BCT had a lower percentage of viability than that of the control at all tested dilutions (p < .0001). Cell migration rates in BD and BCR were similar to those in the control group after 24 h and 48 h (p > .05), whilst BCT had larger voids than the control in both periods (p < .0001). Conclusions: BCR, BCT and BD were associated with tooth discolouration. BCR had the lowest staining values, the highest radiopacity and viability greater than 80% hDPCs.

In Vitro Cytotoxicity Evaluation of A Novel Root Repair Material

Cytotoxicity of Two Dental Materials on Fibroblasts Derived from Human Embryonic Stem Cells

Differential Responses of Human Dental Pulp Stromal Cells to Bioceramic Materials: A Comparative In Vitro Study

An in vitro evaluation of antimicrobial activity of a fast-setting endodontic material

Evaluation of biocompatibility and bioactive potential of Well-Root PT by comparison with ProRoot MTA and Biodentine

Evaluation of Cytotoxicity of the Dental Materials TheraCal LC, TheraCal PT, ApaCal ART and Biodentine Used in Vital Pulp Therapy: In Vitro Study

Biological parameters, discolouration and radiopacity of calcium silicate-based materials in a simulated model of partial pulpotomy

The Effects of Tricalcium-Silicate-Nanoparticle-Containing Cement: In Vitro and In Vivo Studies

Dentine Remineralisation Induced by “Bioactive” Materials through Mineral Deposition: An In Vitro Study

Biocompatibility evaluation of biodentine in subcutaneous tissue of rats

Antibacterial, biocompatible, and mineralization‐inducing properties of calcium silicate‐based cements

Cytotoxicity and osteogenic potential of silicate calcium cements as potential protective materials for pulpal revascularization.

A tricalcium phosphate (TCP) and hydroxyapatite (HA) based light-cured biomaterial for vital pulp therapy

In-vitro-cytotoxicity of self-adhesive dental restorative materials

Evaluation of Surface Microstructure and Compressive Strength of Mineral Trioxide Aggregate and Biodentine in the Existence and Absence of Oral Tissue Fluids

Biocompatibility and pro-mineralization effects of premixed calcium silicate-based materials on human dental pulp stem cells: An in vitro and in vivo study

An In Vitro Stereomicroscopic Evaluation of Bioactivity between Neo MTA Plus, Pro Root MTA, BIODENTINE & Glass Ionomer Cement Using Dye Penetration Method

Cytotoxicity of dilutions of bioceramic materials in stem cells of human exfoliated deciduous teeth

Biocompatibility, bioactive potential, porosity, and interface analysis calcium silicate repair cements in a dentin tube model

Biocompatibility of mineral trioxide aggregate and biodentine as root-end filling materials: an in vivo study

"Biological responses of two calcium-silicate-based cements on a tissue-engineered 3D organotypic deciduous pulp analogue"